Microwave reactor methodologies are unique in their ability to be scaled-up without suffering thermal gradient effects, providing a potentially industrially important improvement in nanocrystal synthetic methodology over convective methods. Synthesis of high-quality, near monodispersity nanoscale InGaP, InP, and CdSe have been prepared via direct microwave heating of the molecular precursors rather than convective heating of the solvent. Microwave dielectric heating not only enhances the rate of formation, it also enhances the material quality and size distributions. The reaction rates are influenced by the microwave field and by additives. The final quality of the microwave-generated materials depends on the reactant choice, the applied power, the reaction time, and temperature. CdSe nanocrystals prepared in the presence of a strong microwave absorber exhibit sharp excitonic features and a QY of 68% for microwave-grown materials. InGaP and InP are rapidly formed at 280 degrees C in minutes, yielding clean reactions and monodisperse size distributions that require no size-selective precipitation and result in the highest out of batch quantum efficiency reported to date of 15% prior to chemical etching. The use of microwave (MW) methodology is readily scalable to larger reaction volumes, allows faster reaction times, removes the need for high-temperature injection, and suggests a specific microwave effect may be present in these reactions.

Conversion reaction cells afford the ability to explore new energy storage paradigms that transcend the dogma of small, low‐charge cations essential to intercalative processes. Here we report the use of earth‐abundant and green calcium and sulfur in unprecedented conversion reaction Ca–S primary cells. Using S‐infiltrated mesoporous carbon (abbreviated S@meso‐C) cathodes, we achieve discharge capacities as high as 600 mAh g−1 (S basis) within the geometry Ca|Ca(ClO4)2/CH3CN|S@meso‐C, at a discharge rate of C/3.5. The electrolyte system in the Ca–S battery is of paramount importance as the solid electrolyte interface (SEI) formed on the Ca anode limits the capacity and stability of the cell. We determine that 0.5 M Ca(ClO4)2 in CH3CN forms an SEI that advantageously breaks down under anodic bias to allow oxidation of the anode. This same SEI, however, exhibits high impedance which increases over time at open circuit limiting the shelf life of the cell.

Sulfur cathodes in conversion reaction batteries offer high gravimetric capacity but suffer from parasitic polysulfide shuttling. We demonstrate here that transition metal chalcogels of approximate formula MoS 3.4 achieve high gravimetric capacity close to 600 mAh g −1 (close to 1000 mAh g −1 on a sulfur-basis), as electrode materials for lithium-ion batteries. Transition metal chalcogels are amorphous, and comprise polysulfide chains connected by inorganic linkers. The linkers appear to act as a "glue" in the electrode to prevent polysulfide shuttling. The Mo chalcogels function as electrodes in carbonate-as well as ether-based electrolytes, which further provides evidence for polysulfide solubility not being a limiting issue. We employ X-ray spectroscopy and operando pair distribution function techniques to elucidate the structural evolution of the electrode. Raman and X-ray photoelectron spectroscopy track the chemical moieties that arise during the anion-redox-driven processes. We find the redox state of Mo remains unchanged across the electrochemical cycling and correspondingly, the redox

The Li-S system offers a tantalizing battery for electric vehicles and renewable energy storage due to its high theoretical capacity of 1675 mAh g(-1) and its employment of abundant and available materials. One major challenge in this system stems from the formation of soluble polysulfides during the reduction of S8, the active cathode material, during discharge. The ability to deploy this system hinges on the ability to control the behavior of these polysulfides by containing them in the cathode and allowing for further redox. Here, we exploit the high surface areas and good electrical conductivity of mesoporous carbons (MC) to achieve high sulfur utilization while functionalizing the MC with sulfur (S-MC) in order to modify the surface chemistry and attract polysulfides to the carbon material. S-MC materials show enhanced capacity and cyclability trending as a function of sulfur functionality, specifically a 50% enhancement in discharge capacity is observed at high cycles (60-100 cycles). Impedance spectroscopy suggests that the S-MC materials exhibit a lower charge-transfer resistance compared with MC materials which allows for more efficient electrochemistry with species in solution at the cathode. Isothermal titration calorimetry shows that the change in surface chemistry from unfunctionalized to S-functionalized carbons results in an increased affinity of the polysulfide intermediates for the S-MC materials, which is the likely cause for enhanced cyclability.