Germanium possesses higher electron and hole mobilities than silicon. There is a big leap, however, between these basic material parameters and implementation for high-performance microelectronics. Here we discuss some of the major issues for Ge metal oxide semiconductor field effect transistors ͑MOSFETs͒. Substrate options are overviewed. A dislocation reduction anneal Ͼ800°C decreases threading dislocation densities for Ge-on-Si wafers 10-fold to 10 7 cm −2 ; however, only a 2 times reduction in junction leakage is observed and no benefit is seen in on-state current. Ge wet etch rates are reported in a variety of acidic, basic, oxidizing, and organic solutions, and modifications of the RCA clean suitable for Ge are discussed. Thin, strained epi-Si is examined as a passivation of the Ge/gate dielectric interface, with an optimized thickness found at ϳ6 monolayers. Dopant species are overviewed. P and As halos are compared, with better short channel control observed for As. Area leakage currents are presented for pϩ/n diodes, with the n-doping level varied over the range relevant for pMOS. Germanide options are discussed, with NiGe showing the most promise. A defect mode for NiGe is reported, along with a fix involving two anneal steps. Finally, the benefit of an end-of-process H 2 anneal for device performance is shown.

No abstract

No abstract

Articles you may be interested inStructural analysis, elemental profiling, and electrical characterization of HfO 2 thin films deposited on In 0.53 Ga 0.47 As surfaces by atomic layer deposition Improvement in bias instabilities of Hf-silicate by dilute hydrochloric acid (500:1) post-deposition rinsing and its effect after high-pressure H 2 anneal Alternative surface passivation on germanium for metal-oxide-semiconductor applications with high-k gate dielectric Appl.

We have studied the thermal stability of HfO2 thin layers on germanium and the substrate interface development. HfO2 was deposited on Ge substrates and annealed in O2 or N2 at 500°C (substrate temperature). After O2 anneal, we observed the formation of hafnium germanate, which is stable at 500°C in N2 as opposed to GeO2 that desorbs as GeO. We believe that this hafnium germanate is an oxygen barrier and as such is at the origin of the much thinner interface between HfO2 and germanium as compared to silicon. In addition, results suggest that the HfGeOx is related to the high interface state density frequently reported for germanium metal oxide semiconductor devices.