Silicon nanopowders were prepared by hot-wire chemical vapour deposition (CVD) from monosilane. Wire materials including Hf, Nb, Ta, Mo, W, Rh, Re, Ir, Pd, and Pt were tested. The filament temperature was varied in the range of 400 -2000°C and pressures between 1.0 -1.5 bar.Products were characterised by bulk elemental analysis and a laser granulometer. The powders were investigated by TG-DSC-MS under inert, O 2 , and H 2 O containing atmosphere, respectively, in a temperature range of 20 -700°C. Hydrogen evolution occurred in three separate steps, depending on the applied gas atmosphere. The oxidation mechanism was explored by the characteristic O x Si-H bands (x = 0 -3) observed in ex situ DRIFT experiments. The oxidation of hydrogen terminated silicon surfaces was investigated employing oxygen (O 2 ), hydrogen peroxide (H 2 O 2 ), permanganate (MnO − 4 ), or peroxodisulfate S 2 O 2− 8 in a temperature range of 0 -120°C. The oxidation was stepwise and strongly enhanced after pretreatment by alkyl lithium salts or Grignard reagents.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.