In the past several years, we have made significant progress in the growth of CdTe buffer layers on Si wafers using molecular beam epitaxy (MBE) as well as the growth of HgCdTe onto this substrate as an alternative to the growth of HgCdTe on bulk CdZnTe wafers. These developments have focused primarily on mid-wavelength infrared (MWIR) HgCdTe and have led to successful demonstrations of high-performance 1024 ϫ 1024 focal plane arrays (FPAs) using Rockwell Scientific's double-layer planar heterostructure (DLPH) architecture. We are currently attempting to extend the HgCdTe-on-Si technology to the long wavelength infrared (LWIR) and very long wavelength infrared (VLWIR) regimes. This is made difficult because the large lattice-parameter mismatch between Si and CdTe/HgCdTe results in a high density of threading dislocations (typically, Ͼ5E6 cm Ϫ2 ), and these dislocations act as conductive pathways for tunneling currents that reduce the R o A and increase the dark current of the diodes. To assess the current state of the LWIR art, we fabricated a set of test diodes from LWIR HgCdTe grown on Si. Silicon wafers with either CdTe or CdSeTe buffer layers were used. Test results at both 78 K and 40 K are presented and discussed in terms of threading dislocation density. Diode characteristics are compared with LWIR HgCdTe grown on bulk CdZnTe.

No abstract

X-ray diffraction full-width at half-maximum (XRD FWHM), reflection highenergy electron diffraction (RHEED), and atomic force microscopy (AFM) indicate a mosaic structure for molecular-beam epitaxy (MBE) (211)B CdTe/Si. AFM measurements indicate long, thin, small-angle-disoriented grains for CdTe/Si epilayers. These disoriented grains are $1 lm in the [111] direction and are $40 nm in the [011] direction. The RHEED pattern in the [111] direction depicts nearly ideal single-crystal periodicity. The RHEED pattern in the [011] direction is indicative of small-angle-disoriented crystalline grains. Scanning electron microscopy (SEM), AFM, and XRD measurements all indicate an approximate factor of 10 increase in the Everson etch pit density (EPD) over standard Nomarski microscopy Everson EPD determination.