Mg-substituted hydroxyapatite (HAp) bioceramic microspheres were prepared by spray drying and subsequent processing at 1173, 1273 and 1373 K. Influence of various Mg substitution levels (up to 0.84 ± 0.10 wt%) on physicochemical properties of the HAp bioceramic microspheres was evaluated. Obtained results were used for the elucidation of the compositional and structural characteristics of the microspheres in conjunction with adsorption of protein, namely, bovine serum albumin (BSA). The primary difference among the microspheres processed at various temperature was the presence or absence of the micropores (< 2 nm in diameter) and mesopores (between 2 and 50 nm). Presence of the micro-and mesopores resulted in higher specific surface area (SSA), enhanced solubility, i.e., ion release, and, accordingly, increase in the amount of BSA adsorbed on the microspheres. Furthermore, the BSA adsorption capacity of the microspheres decreased with increasing Mg content despite of higher SSA.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.