Gelatin/chitosan/poly(vinyl alcohol) (PVA) hydrogels were fabricated with different polymer ratio using the freeze-drying process. The thermal stability, water state, rheological, and cytotoxic properties of the hydrogels were evaluated. Thermogravimetric/differential scanning calorimetry analyses showed a decomposition onset temperature below 242.7 AE 2.7 C. The samples did not show statistical differences (p < 0.05) on the onset temperature values. Nonfreezing water reached a constant value around of 1 g water/g polymer. Freezing water increased linearly with the increase of the water content independently of the polymer ratio. The hydrogels showed an equilibrium water content from 9 to 13 times their mass. The hydrogels exhibited a solid-viscoelastic behavior. The elastic modulus was higher with the increase of chitosan concentration (G 0 = 22 170 AE 85 Pa) independently of the temperature (5-55 C). In vitro assay showed that hydrogels are nontoxic in the HT29-MTX-E12 cell line. These results indicate that the gelatin/chitosan/PVA hydrogels could be considered for biomedical applications.

A nanomechanical testing set-up is developed by integrating an atomic force microscope (AFM) for force measurements with a scanning electron microscope (SEM) to provide imaging capabilities. Electrospun nanofibers of polyvinyl alcohol (PVA), nylon-6 and biological mineralized collagen fibrils (MCFs) from antler bone were manipulated and tensile-tested using the AFM-SEM set-up. The complete stress-strain behavior to failure of individual nanofibers was recorded and a diversity of mechanical properties observed, highlighting how this technique is able to elucidate mechanical behavior due to structural composition at nanometer length scales.

Gelatin/chitosan/polyvinyl alcohol hydrogels were fabricated at different polymer ratios using the freeze-drying and sterilized by steam sterilization. The thermal stability, chemical structure, morphology, surface area, mechanical properties, and biocompatibility of hydrogels were evaluated by simultaneous thermal analysis, Fourier transform infrared spectroscopy, X-ray diffraction, confocal microscopy, adsorption/desorption of nitrogen, rheometry, and 3-4,[5-dimethylthiazol-2-yl]-2,5-diphenyl tetrazolium bromide cell viability assay (MTT assay), respectively. The samples showed a decomposition onset temperature below 253.3 ± 4.8 C, a semicrystalline nature, and a highly porous structure. Hydrogels reached the maximum water uptake in phosphate-buffered saline after 80 min, showing values from nine to twelve times their dry mass. Also, hydrogels exhibiting a solid-like behavior ranging from 2,567 ± 467 to 48,705 ± 2,453 Pa at 0.1 rad/s (low frequency). The sterilized hydrogels showed low cytotoxicity (cell viability > 70%) to the HT29-MTX-E12 cell line. Sterilized hydrogels by steam sterilization can be good candidates as scaffolds for tissue engineering applications. K E Y W O R D Schitosan, hydrogels, porosity, swelling behavior, viscoelastic properties

Modelado de la biodegradación en biorreactores de lodos de hidrocarburos totales del petróleo intemperizados en suelos y sedimentos (Biodegradation modeling of sludge bioreactors of total petroleum hydrocarbons weathering in soil and sediments)

No abstract