The kinetics of emulsion polymerization of monomers MMA/BA was studied to investigate the effect of cross-linkable monomer PPGDA. The results showed that by the incorporation of PPGDA, rate constant of reaction decreased. The IR and differential scanning calorimetry were used to characterize the presence of PPGDA in the synthesized polymers. These polymers were coated on glass panels and cured at appropriate temperature. The results showed that the polymer containing 15 wt % PPGDA had minimum value of Fickian diffusion coefficient, thus showing highest level of cross-linking among all the polymers studied.
The emulsion polymerization of the monomers methyl methacrylate (MMA) and 2-ethylhexyl acrylate (EHA) was studied to investigate the effect of the crosslinkable monomer poly(propylene glycol diacrylate) (PPGDA). IR spectroscopy, NMR, differential scanning calorimetry, gel permeation chromatography, and scanning electron microscopy were used to characterize the synthesized polymers. These polymers were coated on glass panels and cured at appropriate temperatures to study the physical properties, swelling behavior, surface tension, and contact angle of these polymer latices. The results show that as the concentration of EHA monomer increased, the surface tension of the latices decreased. The copolymers were characterized by 1 H-NMR spectroscopy to ensure the absence of unreacted monomer, and the results confirm the incorporation of EHA units in the copolymer. The contact angle of the latices on the glass substrate was smaller than that on the metal. The swelling mechanism of the film showed that the Fickian diffusion coefficient with 10 wt % PPGDA was at a minimum value and was the most highly crosslinked polymer among the samples. V C 2011 Wiley Periodicals, Inc. J Appl Polym Sci 122: [676][677][678][679][680][681][682][683][684] 2011
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.