In this study, hyaluronic acid (HA) was electro-spun and electro-blown to prepare nonwoven nanofibrous membranes. Critical parameters for processing and corresponding effects on the membrane morphology were investigated using the methods of rheology and scanning electron microscopy (SEM). During electro-spinning, the optimal HA concentration window for nanofibrous formation was determined within a narrow range of 1.3-1.5 w/v %, corresponding to a solution viscosity range of 3-30 Pa s at a shear rate of 1 s(-1). SEM results indicated that, with increases in (1) the total concentration by blending of low molecular weight HA, (2) the evaporation rate by the addition of ethanol, and/or (3) the feeding rate of solution, the electro-spinning performance for creating nanofibers was improved. However, the improvement was not sufficient to achieve a consistent production of high quality nonwoven nanofiber membranes. This problem was overcome by a new electro-blowing process using the combination of air flow and electro-spinning. Although air blowing at room temperature around the spinneret orifice did not exhibit a remarkable enhancement of nanofiber formation of HA, the performance was significantly improved with an increase in the air blowing rate. SEM results showed that the temperature of air-blowing was the most effective parameter in ensuring HA nanofiber formation. As the temperature of the blown air increased from 25 to 57 degrees C, the nanofiber formation became consistent and uniform. A high quality HA nonwoven membrane of nanofibers was successfully produced by blowing air at 57 degrees C with a 70 ft(3)/hr flow rate.

Silk fibroin/chitosan blend films were examined through IR spectroscopy to determine the conformational changes of silk fibroin. The effects of the fibroin/chitosan blend ratios (chitosan content) on the physical and mechanical properties were investigated to discover the feasibility of using these films as biomedical materials such as artificial skin and wound dressing. The mechanical properties of the blend films containing 10 -40% chitosan were found to be excellent. The tensile strength, breaking elongation, and Young's modulus were affected by the chitosan contents of the blend films, which were also related to the density and degree of swelling. The coefficient of water vapor permeability of the blend films increased linearly with the chitosan content, and the values of 1000 -2000 g m Ϫ2 day Ϫ1 were comparable to those of commercial wound dressings. Silk fibroin/chitosan blend films had good oxygen and water vapor permeabilities, making them useful as biomaterials. In particular, the blend film containing 40 -50% chitosan showed very high oxygen permeability.

No abstract

No abstract

No abstract

No abstract