Detection in short-wave infrared (SWIR) has become a very stringent technology requirement for developing fields like hyperspectral imaging or climate changes. In a market dominated by III–V materials, GeSn, a Si compatible semiconductor, has the advantage of cost efficiency and inerrability by using the mature Si technology. Despite the recent progress in material growth, the easy fabrication of crystalline GeSn still remains a major challenge, and different methods are under investigation. We present the formation of GeSn nanocrystals (NCs) embedded in oxide matrix and their SWIR characterization. The simple and cost-effective fabrication method is based on thermal treatment of amorphous (Ge1–x Sn x ) y (SiO2)1–y layers deposited by magnetron sputtering. The nanocrystallization for Ge1–x Sn x with 9–22 at. % Sn composition in SiO2 matrix with 9% to 15% mole percent was studied under low thermal budget annealing in the 350–450 °C temperature range. While the Sn at.% content is the main parameter influencing the band-structure of the NCs, the SWIR sensitivity can be optimized by SiO2 content and H2 gas component in the deposition atmosphere. Their role is not only changing the crystallization parameters but also to reduce the carrier recombination by passivation of NCs defects. The experiments indicate a limited composition dependent temperature range for GeSn NCs formation before β-Sn phase segregation occurs. NCs with an average size of 6 nm are uniformly distributed in the film, except the surface region where larger GeSn NCs are formed. Spectral photovoltaic current measured on SiO2 embedded GeSn NCs deposited on p-Si substrate shows extended SWIR sensitivity up to 2.4 μm for 15 at. % Sn in GeSn NCs. The large extension of the SWIR detection is a result of many factors related to the growth parameters and also to the in situ or ex situ annealing procedures that influence the uniformity and size distribution of NCs.
Si and Ge nanocrystals in oxides are of a large interest for photo-effect applications due to the fine-tuning of the optical bandgap by quantum confinement in nanocrystals. In this work, dense Ge nanocrystals suitable for enhanced photoconduction were fabricated from 60% Ge in TiO2 amorphous layers by low temperature rapid thermal annealing at 550 °C. An exponential increase of the photocurrent with the applied voltage was observed in coplanar structure of Ge nanocrystals composite films deposited on oxidized Si wafers. The behaviour was explained by field effect control of the Fermi level at the Ge nanocrystals-TiO2 layer/substrate interfaces. The blue-shift of the absorption gap from bulk Ge value to 1.14 eV was evidenced in both photocurrent spectra and optical reflection-transmission experiments, in good agreement with quantum confinement induced bandgap broadening in Ge nanocrystal with sizes of about 5 nm as found from HRTEM and XRD investigations. A nonmonotonic spectral dependence of the refractive index is associated to the Ge nanocrystals formation. The nanocrystal morphology is also in good agreement with the Coulomb gap hopping mechanism of T–1/2 -type explaining the temperature dependence of the dark conduction.
The development of short-wave infrared (SWIR) photonics based on GeSn alloys is of high technological interest for many application fields, such as the Internet of things or pollution monitoring. The manufacture of crystalline GeSn is a major challenge, mainly because of the low miscibility of Ge and Sn. The use of embedded GeSn nanocrystals (NCs) by magnetron sputtering is a cost-effective and efficient method to relax the growth conditions. We report on the use of GeSn/SiO2 multilayer deposition as a way to control the NC size and their insulation. The in situ prenucleation of NCs during deposition was followed by ex situ rapid thermal annealing. The nanocrystallization of 20×(11nm_Ge0.865Sn0.135/1.5nm_SiO2) multilayers leads to formation of GeSn NCs with ∼16% Sn concentration and ∼9 nm size. Formation of GeSn domes that are vertically correlated contributes to the nanocrystallization process. The absorption limit of ∼0.4 eV in SWIR found by ellipsometry is in agreement with the spectral photosensitivity. The ITO/20×(GeSn NC/SiO2)/p-Si/Al diodes show a maximum value of the SWIR photosensitivity at a reverse voltage of 0.5 V, with extended sensitivity to wavelengths longer than 2200 nm. The multilayer diodes have higher photocurrent efficiency compared to diodes based on a thick monolayer of GeSn NCs.
Trilayer memory capacitors of control HfO2/floating gate of Ge nanoparticles in HfO2/tunnel HfO2/Si substrate deposited by magnetron sputtering and subsequently annealed are investigated for the first time for applications in radiation dosimetry. In the floating gate (FG), amorphous Ge nanoparticles (NPs) are arranged in two rows inside the HfO2 matrix. The HfO2 matrix is formed of orthorhombic/tetragonal nanocrystals (NCs). The adjacent thin films to the FG are also formed of orthorhombic/tetragonal HfO2 NCs. This phase is formed during annealing, in samples with thick control HfO2, in the presence of Ge, being induced by the stress. In the rest of the control oxide, HfO2 NCs are monoclinic. Orthorhombic HfO2 has ferroelectric properties and therefore enhances the memory window produced by charge storage in Ge NPs to above 6 V. The high sensitivity of 0.8 mV Gy−1 to α particle irradiation from a 241Am source was measured by monitoring the flatband potential during radiation exposure after electrical writing of the memory.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.