Crystal phase regulations may endow materials with enhanced or new functionalities. However, syntheses of noble metal-based allomorphic nanomaterials are extremely difficult, and only a few successful examples have been found. Herein, we report the discovery of hexagonal close-packed Pt–Ni alloy, despite the fact that Pt–Ni alloys are typically crystallized in face-centred cubic structures. The hexagonal close-packed Pt–Ni alloy nano-multipods are synthesized via a facile one-pot solvothermal route, where the branches of nano-multipods take the shape of excavated hexagonal prisms assembled by six nanosheets of 2.5 nm thickness. The hexagonal close-packed Pt–Ni excavated nano-multipods exhibit superior catalytic property towards the hydrogen evolution reaction in alkaline electrolyte. The overpotential is only 65 mV versus reversible hydrogen electrode at a current density of 10 mA cm−2, and the mass current density reaches 3.03 mA μgPt−1 at −70 mV versus reversible hydrogen electrode, which outperforms currently reported catalysts to the best of our knowledge.
Developing active and durable electro-catalysts toward ethanol oxidation reaction (EOR) with high selectivity toward the C-C bond cleavage is an important issue for the commercialization of direct ethanol fuel cell. Unfortunately, current ethanol oxidation electro-catalysts (e.g., Pt, Pd) still suffer from poor selectivity for direct oxidation of ethanol to CO, and rapid activity degradation. Here we report a facile route to the synthesis of a new kind of cyclic penta-twinned (CPT) Rh nanostructures that are self-supported nanobranches (NBs) built with 1-dimension CPT nanorods as subunits. Structurally, the as-prepared Rh NBs possess high percentage of open {100} facets with significant CPT-induced lattice strains. With these unique structural characteristics, the as-prepared CPT Rh NBs exhibit outstanding electrocatalytic performance toward EOR in alkaline solution. Most strikingly, the selectivity of complete conversion ethanol to CO on the CPT Rh NBs is measured to be as high as 14.5 ± 1.1% at -0.15 V, far exceeding that for single-crystal tetrahedral nanocrystals, icosahedral nanocrystals, and commercial Rh black, as well as majority of reported values for Pt or Pd-based electro-catalysts. By combining with density functional theory calculation, the effects of different structural features of Rh on EOR are definitively elucidated. It was found that the large amount of open Rh (100) facets dominantly contribute to the outstanding activity and exceptionally high selectivity, while the additional tensile strain on (100) planes can further boost the catalytic activity by enhancing the adsorption strength and lowering the reaction barrier of dehydrogenation process of ethanol. As a proof of concept, the present work shows that rationally optimizing surface and electronic structure of electro-catalysts by simultaneously engineering their surface and bulk structures is a promising strategy to promote the performance of electro-catalysts.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.