Crystal phase regulations may endow materials with enhanced or new functionalities. However, syntheses of noble metal-based allomorphic nanomaterials are extremely difficult, and only a few successful examples have been found. Herein, we report the discovery of hexagonal close-packed Pt–Ni alloy, despite the fact that Pt–Ni alloys are typically crystallized in face-centred cubic structures. The hexagonal close-packed Pt–Ni alloy nano-multipods are synthesized via a facile one-pot solvothermal route, where the branches of nano-multipods take the shape of excavated hexagonal prisms assembled by six nanosheets of 2.5 nm thickness. The hexagonal close-packed Pt–Ni excavated nano-multipods exhibit superior catalytic property towards the hydrogen evolution reaction in alkaline electrolyte. The overpotential is only 65 mV versus reversible hydrogen electrode at a current density of 10 mA cm−2, and the mass current density reaches 3.03 mA μgPt−1 at −70 mV versus reversible hydrogen electrode, which outperforms currently reported catalysts to the best of our knowledge.

Developing active and durable electro-catalysts toward ethanol oxidation reaction (EOR) with high selectivity toward the C-C bond cleavage is an important issue for the commercialization of direct ethanol fuel cell. Unfortunately, current ethanol oxidation electro-catalysts (e.g., Pt, Pd) still suffer from poor selectivity for direct oxidation of ethanol to CO, and rapid activity degradation. Here we report a facile route to the synthesis of a new kind of cyclic penta-twinned (CPT) Rh nanostructures that are self-supported nanobranches (NBs) built with 1-dimension CPT nanorods as subunits. Structurally, the as-prepared Rh NBs possess high percentage of open {100} facets with significant CPT-induced lattice strains. With these unique structural characteristics, the as-prepared CPT Rh NBs exhibit outstanding electrocatalytic performance toward EOR in alkaline solution. Most strikingly, the selectivity of complete conversion ethanol to CO on the CPT Rh NBs is measured to be as high as 14.5 ± 1.1% at -0.15 V, far exceeding that for single-crystal tetrahedral nanocrystals, icosahedral nanocrystals, and commercial Rh black, as well as majority of reported values for Pt or Pd-based electro-catalysts. By combining with density functional theory calculation, the effects of different structural features of Rh on EOR are definitively elucidated. It was found that the large amount of open Rh (100) facets dominantly contribute to the outstanding activity and exceptionally high selectivity, while the additional tensile strain on (100) planes can further boost the catalytic activity by enhancing the adsorption strength and lowering the reaction barrier of dehydrogenation process of ethanol. As a proof of concept, the present work shows that rationally optimizing surface and electronic structure of electro-catalysts by simultaneously engineering their surface and bulk structures is a promising strategy to promote the performance of electro-catalysts.

We report a facile synthesis of Ag nanocubes with concave side faces and Au-Ag alloy frames, namely Ag@Au-Ag concave nanocrystals, by titrating HAuCl solution into an aqueous mixture of Ag nanocubes, ascorbic acid (HAsc), NaOH, and cetyltrimethylammonium chloride (CTAC) at an initial pH of 11.6 under ambient conditions. Different from all previous studies involving poly(vinylpyrrolidine), the use of CTAC at a sufficiently high concentration plays an essential role in carving away Ag atoms from the side faces through galvanic replacement. Concurrent co-deposition of Au and Ag atoms via chemical reduction at orthogonal sites on the surface of Ag nanocubes leads to the generation of Ag@Au-Ag concave nanocrystals with well-defined and controllable structures. Specifically, in the presence of CTAC-derived Cl ions, the titrated HAuCl is maintained in the AuCl species, enabling its galvanic replacement with the Ag atoms located on the side faces of nanocubes. The released Ag ions can be retained in the soluble form of AgCl by complexing with the Cl ions. Both the AuCl and AgCl in the solution are then reduced by ascorbate monoanion, a product of the neutralization reaction between HAsc and NaOH, to Au and Ag atoms for their preferential co-deposition onto the edges and corners of the Ag nanocubes. Compared with Ag nanocubes, the Ag@Au-Ag concave nanocrystals exhibit much stronger SERS activity at an excitation of 785 nm, making it feasible to monitor the Au-catalyzed reduction of 4-nitrothiophenol by NaBH in situ. When the Ag cores are removed, the concave nanocrystals evolve into Au-Ag nanoframes with controllable ridge thicknesses.