Transparent electrodes of tin dioxide (SnO2) on glasses were further wet-etched in the diluted HCl:Cr solution to obtain larger surface roughness and better light-scattering characteristic for thin-film solar cell applications. The process parameters in terms of HCl/Cr mixture ratio, etching temperature, and etching time have been investigated. After etching process, the surface roughness, transmission haze, and sheet resistance of SnO2glasses were measured. It was found that the etching rate was increased with the additions in etchant concentration of Cr and etching temperature. The optimum texture-etching parameters were 0.15 wt.% Cr in 49% HCl, temperature of 90°C, and time of 30 sec. Moreover, silicon thin-film solar cells with the p-i-n structure were fabricated on the textured SnO2glasses using hot-wire chemical vapor deposition. By optimizing the texture-etching process, the cell efficiency was increased from 4.04% to 4.39%, resulting from the increment of short-circuit current density from 14.14 to 15.58 mA/cm2. This improvement in cell performances can be ascribed to the light-scattering effect induced by surface texturization of SnO2.
One of the most challenging problems to develop polycrystalline silicon thin-film solar
cells is the growth of crystalline silicon on foreign, low-cost and low-temperature substrates. In this paper, a laser doping technique was developed for the plasma-deposited amorphous silicon film. A process combination of recrystallization and dopant diffusion (phosphorous or boron) was achieved simultaneously by the laser annealing process. The doping precursor was synthesized by a sol-gel
method and was spin-coated on the sample. After laser irradiation, the grain size of the doped polycrystalline silicon was examined to be about 0.5~1.0 µm. The concentrations of 2×1019 and 5× 1018 cm-3 with Hall mobilities of 92.6 and 37.5 cm²/V-s were achieved for the laser-diffused phosphorous- and boron-type polysilicon films, respectively.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.