The aim of the study was to examine the role of composition, inclusions, and precipitates on the pitting corrosion resistance of Mn-alloyed austenitic stainless steels. The pitting corrosion measurements were conducted in three electrolytes: sea water (3.56 wt% NaCl), sulfuric acid (0.5M H 2 SO 4 ), and sulfuric acid þ salt (0.5 M H 2 SO 4 þ 0.4 M NaCl) solutions. In the tests, it was observed that manganese sulfides act as corrosion pit initiators. As the Cr content was decreased and Ni partially replaced by Mn, the pitting corrosion resistance was reduced in seawater and H 2 SO 4 þ NaCl solutions. On the other hand, the amount of inclusions was not found to have a clear correlation to the potential at which the corrosion pits initiate. In the sulfuric acid solution, no pitting was observed and all the materials exhibited similar behavior in the passive range. However, in the transpassive range the dissolution rate of AISI 304 steel was greatest, whereas more Mn and less Ni and Cr containing steels exhibited a secondary passivation behavior.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.