Large magnetic-field-induced strains have been observed in Heusler alloys with a body-centred cubic ordered structure and have been explained by the rearrangement of martensite structural variants due to an external magnetic field. These materials have attracted considerable attention as potential magnetic actuator materials. Here we report the magnetic-field-induced shape recovery of a compressively deformed NiCoMnIn alloy. Stresses of over 100 MPa are generated in the material on the application of a magnetic field of 70 kOe; such stress levels are approximately 50 times larger than that generated in a previous ferromagnetic shape-memory alloy. We observed 3 per cent deformation and almost full recovery of the original shape of the alloy. We attribute this deformation behaviour to a reverse transformation from the antiferromagnetic (or paramagnetic) martensitic to the ferromagnetic parent phase at 298 K in the Ni45Co5Mn36.7In13.3 single crystal.
Ferromagnetic shape memory alloys with a body-centered-cubic ordered structure in a Ni–Ga–Fe system have been developed. The alloys with the composition range of Ni 27 at. % Ga (20–22 at. %)Fe exhibit a thermoelastic martensitic transformation from a B2 and/or an L21 parent to a martensite phase, with a seven-layer modulated (14M) and a five-layer modulated (10M) structure, in the ferromagnetic state. The parent phase transforms from the B2 to the L21 structure at about 970 K during cooling, and the degree of the L21 order in the parent phase is increased by annealing at 773 K, resulting in the increase of both the martensite starting and the Curie temperatures. The ductility of these alloys is improved by introducing of a small amount of a γ-phase solid solution. Consequently, we can conclude that the present alloys are promising for ferromagnetic shape memory alloys.
Shape memory and magnetic properties of a Ni43Co7Mn39Sn11 Heusler polycrystalline alloy were investigated by differential scanning calorimetry, the sample extraction method, and the three-terminal capacitance method. A unique martensitic transformation from the ferromagnetic parent phase to the antiferromagneticlike martensite phase was detected and magnetic-field-induced “reverse” transition was confirmed in a high magnetic field. In addition, a large magnetic-field-induced shape recovery strain of about 1.0% was observed to accompany reverse martensitic transformation, and the metamagnetic shape memory effect, which was firstly reported in a Ni45Co5Mn36.7In13.3 Heusler single crystal, was confirmed in a polycrystalline specimen.
Lithium-ion batteries (LIBs) are generally constructed by lithium-including positive electrode materials, such as LiCoO2, and lithium-free negative electrode materials, such as graphite. Recently, lithium-free positive electrode materials, such as sulfur, are gathering great attention from their very high capacities, thereby significantly increasing the energy density of LIBs. Though the lithium-free materials need to be combined with lithium-containing negative electrode materials, the latter has not been well developed yet. In this work, the feasibility of Li-rich Li-Si alloy is examined as a lithium-containing negative electrode material. Li-rich Li-Si alloy is prepared by the melt-solidification of Li and Si metals with the composition of Li21Si5. By repeating delithiation/lithiation cycles, Li-Si particles turn into porous structure, whereas the original particle size remains unchanged. Since Li-Si is free from severe constriction/expansion upon delithiation/lithiation, it shows much better cyclability than Si. The feasibility of the Li-Si alloy is further examined by constructing a full-cell together with a lithium-free positive electrode. Though Li-Si alloy is too active to be mixed with binder polymers, the coating with carbon-black powder by physical mixing is found to prevent the undesirable reactions of Li-Si alloy with binder polymers, and thus enables the construction of a more practical electrochemical cell.
The magnetocrystalline anisotropy in a single-crystal Co37Ni34Al29 ferromagnetic shape-memory alloy has been investigated. The prestrain was applied to the parent phase in order to nucleate the specific variant in the sample cooled down through the martensitic transformation temperature. The applied magnetic field facilitates the growth of variants parallel to the applied magnetic field in analogy with the prestrain. From these results of selective nucleation of variants, the magnetocrystalline anisotropy energy in the single crystal Co37Ni34Al29 β′ martensite phase is estimated to be 3.9×106 erg/cm3. In the single crystal, the observed magnitude of the reversible magnetic-field-induced strains is 0.06%.
To obtain a large strain for Ni–Fe–Ga ferromagnetic shape memory alloys, the Curie temperature was increased by adding Co, and the magnetic-field-induced strain (MFIS) has been investigated under static stresses. The magnetocrystalline anisotropy constant K is increased by the addition of Co, and Ni49Fe18Ga27Co6 alloy gives a relatively large value of 1.15×106erg∕cm3 at 300K. From the stress-strain curves for this alloy, the twinning stress is estimated to be 8–9MPa. Consequently, the Ni49Fe18Ga27Co6 alloy exhibits a large MFIS of about 8.5% at room temperature under a static compressive stress of about 8MPa.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.