Organic-inorganic hybrid perovskite solar cells have generated wide interest due to the rapid development of their photovoltaic conversion efficiencies. However, the majority of the reported devices have been fabricated via spin coating with a device area of < 1 cm 2. In this study, we fabricated a wide-bandgap formamidinium lead bromide (FAPbBr 3) film using a cost-effective, high-yielding doctor-blade-coating process. The effects of different surfactants, such as l-α-phosphatidylcholine, polyoxyethylene sorbitan monooleate, sodium lauryl sulfonate, and hexadecyl trimethyl ammonium bromide, were studied during the printing process. Accompanying the optimization of the blading temperature, crystal sizes of over 10 mm and large-area perovskite films of 5 cm  5 cm were obtained using this method. The printed FAPbBr 3 solar cells exhibited a short-circuit current density of 8.22 mA/cm 2 , an open-circuit voltage of 1.175 V, and an efficiency of 7.29%. Subsequently, we replaced the gold with silver nanowires as the top electrode to prepare a semitransparent perovskite solar cell with an average transmittance (400-800 nm) of 25.42%, achieving a highpower efficiency of 5.11%. This study demonstrates efficient doctor-blading printing for preparing large-area FAPbBr 3 films that possess high potential for applications in building integrated photovoltaics.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.