No abstract

Two different chitosan (CS) nanocarriers namely nanoparticles and nanoemulsion were developed to prolong Indomethacin (IM) precorneal residence time and to improve its ocular bioavailability the main limitations in its management of post-operative inflammation and intraocular irritation after cataract extraction. CS-nanoparticles were developed by modified ionic gelation of CS with tripolyphosphate while nanoemulsion was prepared by spontaneous emulsification technique. Transmission electron microscopy revealed regular well-identified spherical shape. The nanoparticles had a mean size of 280 nm, a zeta potential of + 17 mV and high loading efficiency of 84.8 % while the mean size of nanoemulsion was affected by the nature of the surfactant used and varies between 220-690 nm. In vitro release studies, performed under sink conditions, revealed small initial burst release during the first hour followed by slow gradual drug release of 76 and 86% from nanoparticles and nanoemulsion respectively during a 24 h period. In vivo studies and histopathological examination revealed that eyes of rabbits treated with nanoemulsion showed clearer healing of corneal chemical ulcer with moderate effective inhibition of polymorph nuclear leukocytic infiltration (PMNLs) compared with nanoparticles preparation. Moreover, following topical instillation of CS-nanoemulsion to rabbits, it was possible to achieve therapeutic concentration of IM in the cornea through out the duration of the study and fairly high IM level in inner ocular structure, aqueous humor. These levels were significantly higher than those obtained following instillation of IM solution. Therefore, CS nanocarriers developed in this study were able to contact intimately with the cornea providing slow gradual IM release with long-term drug level thereby increasing delivery to both external and internal ocular tissues.

No abstract

No abstract

No abstract

No abstract

The present study suggests that VCM incorporation into SLNs is successfully achievable; however, further studies with different nanoencapsulation materials and techniques would be valuable for improving VCM encapsulation.

The effect of interpolymer complex formation between positively charged chitosan and negatively charged gelatin (Type B) on the release behavior of tramadol hydrochloride from biodegradable chitosan-gelatin sponges was studied. Mixed sponges were prepared by freeze-drying the cross-linked homogenous stable foams produced from chitosan and gelatin solutions where gelatin acts as a foam builder. Generation of stable foams was optimized where concentration, pH of gelatin solution, temperature, speed and duration of whipping process, and, chitosan-gelatin ratio drastically affect the properties and the stability of the produced foams. The prepared sponges were evaluated for their morphology, drug content, and microstructure using scanning electron microscopy, mechanical properties, uptake capacity, drug release profile, and their pharmacodynamic activity in terms of the analgesic effect after implantation in Wistar rats. It was revealed that whipping 7% (w/w) gelatin solution, of pH 5.5, for 15 min at 25 degrees C with a stirring speed of 1000 rpm was the optimum conditions for stable gelatin foam generation. Moreover, homogenous, uniform chitosan-gelatin foam with small air bubbles were produced by mixing 2.5% w/w chitosan solution with 7% w/w gelatin solution in 1:5 ratio. Indeed, polyionic complexation between chitosan and gelatin overcame the drawbacks of chitosan sponge mechanical properties where, pliable, soft, and compressible sponge with high fluid uptake capacity was produced at 25 degrees C and 65% relative humidity without any added plasticizer. Drug release studies showed a successful retardation of the incorporated drug where the t50% values of the dissolution profiles were 0.55, 3.03, and 4.73 hr for cross-linked gelatin, un-cross-linked chitosan-gelatin, and cross-linked chitosan-gelatin sponges, respectively. All the release experiments followed Higuchi's diffusion mechanism over 12 hr. The achieved drug prolongation was a result of a combined effect of both cross-linking and polyelectrolyte complexation between chitosan and gelatin. The analgesic activity of the implanted tramadol hydrochloride mixed chitosan-gelatin sponge showed reasonable analgesic effect that was maintained for more than 8 hr. Therefore, the use of chitosan and gelatin together appears to allow the formulator to manipulate both the drug release profiles and the mechanical properties of the sponge that could be effectively implanted.