No abstract

No abstract

Silicone rubber (SR)/vinyl-graphene oxide (vinyl-GO) nanocomposites were prepared through the hydrosilylation reaction of silicon hydrogen polydimethylsiloxane (H-PDMS) with vinyl polydimethylsiloxane (vinyl-PDMS), in which vinyl-GO was used as a nano filler. The thermally conductive and antistatic properties of the nanocomposites, and their tensile strength and thermal stability were evaluated. The thermally conductive and antistatic properties increased naturally when the nanocomposites had eight to nine parts of vinyl-GO. The addition of 9 parts of vinyl-GO increased the thermal conductivity to 0.44 from 0.17 W/m−1·K−1 of neat SR and the surface resistance value to 108 from 1014 Ω of neat SR. Vinyl-GO is effective in improving the tensile strength and toughness of the nanocomposites. The tensile strength and elongation at break of the nanocomposites were much higher than that of neat SR, especially for 10 parts of vinyl-GO in the nanocomposite, and the tensile strength was 1.84 MPa and the elongation at break was 314.1%. Additionally, compared with neat SR, the nanocomposites had a much higher thermal stability. For eight parts of vinyl-GO in the nanocomposites, H-PDMS with the selected silicon hydrogen content and vinyl-PDMS with the selected vinyl content could offer an appropriate cross-linking degree that suits the character of GO. When the nanocomposite had eight parts of vinyl-GO, its scanning electron microscope exhibited a monolayer GO with folded, twisted, and local surface folds. However, there was a certain amount of multilayer aggregation of GO for 10 parts of vinyl-GO in the nanocomposite.

Realizing a high color rendering index (CRI) in Ce:LuAG transparent ceramics (TCs) with desired thermal stability is essential to their applications in white LEDs/LDs as color converters. In this study, based on the scheme of configuring the red component by Cr3+ doping, an efficient spectral regulation was realized in Ce,Cr:LuAG TCs. A unilateral shift phenomenon could be observed in both photoluminescence (PL) and photoluminescence excitation (PLE) spectra of TCs. By constructing TC-based white LED/LD devices in a remote excitation mode, luminescence properties of Ce,Cr:LuAG TCs were systematically investigated. The CRI values of Ce:LuAG TC based white LEDs could be increased by a magnitude of 46.2%. Particularly, by combining the as fabricated Ce,Cr:LuAG TCs with a 0.5 at% Ce:YAG TC, surprising CRI values of 88 and 85.5 were obtained in TC based white LEDs and LDs, respectively. Therefore, Ce,Cr:LuAG TC is a highly promising color convertor for high-power white LEDs/LDs applied in general lighting and displaying.

In this paper, two trophic lakes: Lake Taihu and Lake Yanghe, and three alpine lakes: Lake Qinghai, Lake Keluke, and Lake Tuosu, were investigated to discover the connections between environmental factors and the phytoplankton community in lakes with differences in trophic levels and climatic conditions. Three seasonal data, including water quality and phytoplankton, were collected from the five lakes. The results demonstrated clear differences in water parameters and phytoplankton compositions in different lakes. The phytoplankton was dominated by Bacillariophyta, followed by Cyanobacteria and Chlorophyta in Lake Qinghai, Lake Keluke, and Lake Tuosu. It was dominated by Cyanobacteria (followed by Chlorophyta and Bacillariophyta in Lake Yanghe) and Cyanobacteria (followed by Chlorophyta and Cryptophyta in Lake Taihu). The temperature was an essential factor favoring the growth of Cyanobacteria, Chlorophyta, and Bacillariophyta, especially Cyanobacteria and Chlorophyta. The pH had significantly negative relationships with Cyanobacteria, Chlorophyta, and Bacillariophyta. Particularly, a high pH might be a strong and negative factor for phytoplankton growth in alpine lakes. A high salinity was also an adverse factor for phytoplankton. Those results could provide fundamental information about the phytoplankton community and their correlated factors in the alpine lakes of the Tibetan Plateau, contributing to the protection and management of alpine lakes.

No abstract

Purpose This study aims to reduce the harm of industrial lubricants to consumers. Composite aluminum-based grease (CAG) was prepared, and medical-grade montmorillonite (M-MMT) was used to improve the antiwear performance of the prepared grease. Design/methodology/approach The influence of the additive (M-MMT) on the tribological performance is mainly investigated using a ball-disc wear tester, and the wear scar surface about the disc was characterized by white light interferometer and electrochemical workstation. Moreover, the cell viability test was used to evaluate the safety of the grease. Findings The results indicated that for the grease containing 1.5% M-MMT, the average coefficient of friction was reduced by about 46% compared with the CAG, the wear volume of the disc reduced by about 74%. Moreover, CAG and 1.5% M-MMT-containing CAG were proved safety by means of the cell viability test. Originality/value The integral properties of CAG can be improved with the medical-grade materials as the additives, while ensuring the safety.

No abstract