Purpose
In this work, Cr3C2-25NiCr coatings were deposited on 410 stainless steel substrate by using the atmospheric plasma spray technique, at varying spaying parameters. The porosity and microhardness, adhesion strength and corrosion behaviour of coatings were examined in relation to these spraying parameters.
Design/methodology/approach
The microstructure of prepared coatings was examined by using scanning electron microscopy. The coating compositional analysis was performed by using X-ray diffraction (XRD) technique. The corrosion resistance of coated steel was investigated by potentiodynamic polarization. Results indicate that optimal factors for minimalizing the porosity were as follows: 10 g/min feed rate, 600 A plasma current and 100 mm spraying distance. The spraying factors influencing corrosion resistance of coating were also evaluated.
Findings
Under this optimal condition, the porosity of coating reached its minimal value of 3.1 per cent. The microhardness and adhesion of coatings also reached their maximum values of 64.8 Rockwell Hardness scale C and 60 MPa, respectively. XRD results indicated the transformation of Cr3C2 originating from Cr3C2-25NiCr source powder into Cr7C3 and Cr23C6 crystalline phases, due to the high temperature during spraying process. The undetectable Cr3C2 peaks indicating that this phase was remained in coating at very low concentrations. The potentiodynamic polarization and salt spray tests confirmed the highest corrosion resistance for the coating prepared by optimal spraying parameters.
Originality/value
The application of Cr3C2-NiCr cermet carbit coating for protection of steel from corrosion-erosion is very promising.
A typical structure of thermal spray coatings consisted of molten particles, semi-molten particles, oxides, pores and cracks. These factors caused the porosity of sprayed coatings, leading to a great influence on the coating properties, especially their wear-corrosion resistance. In this study, a post-spray sealing treatment of Cr3C2-NiCr/Al2O3-TiO2 plasma sprayed coatings was carried out, then their corrosion properties were evaluated, before and after the treatment. For sealing process, aluminum phosphate (APP) containing aluminum oxide (Al2O3) nanoparticles (~10 nm) was used. The permeability of APP into the sprayed coating was analyzed by scanning electron microscopy coupled with energy dispersive spectroscopy (SEM-EDS). The treatment efficiency for porosity and corrosion resistance of sprayed coatings were evaluated by electrochemical measurements, such as the potentiodynamic polarization and electrochemical impedance spectroscopy. In addition, the wear-corrosion resistance of the sealed coating was examined in 3.5 wt.% NaCl circulation solution containing 0.25 wt.% SiO2 particles. The obtained results showed that APP penetrated deeply through the sprayed coating. The incorporation of Al2O3 nanoparticles into APP sealant enhanced the treatment efficiency of porosity for sprayed coating. The effect of the post-treatment on corrosion protection of the sprayed coating has been discussed.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.