Background The aim of this study was (1) to determine and compare the shear bond strength (SBS) of a bioactive composite “Activa Bioactive Restorative” with and without bonding agent and a nanocomposite “Filtek Z350 XT/Z350” and (2) to measure and compare the amount of fluoride release from a bioactive composite “Activa Bioactive Restorative” and a glass ionomer ”Equia forte”. Material and Methods Forty two dentin surfaces from freshly extracted human molars were prepared for shear bond strength testing. The specimens were randomly divided into three equal groups. The restorative materials were applied to all dentin surfaces according to the manufacturer’s instructions, using a special jig (Ultradent) in the following manner : Group 1 (Activa Bioactive Restorative with adhesive), Group 2 (Activa Bioactive Restorative without adhesive) and Group 3 (Filtek Z350 XT/Z350). The bonded specimens were subjected to thermocycling in 5°C and 55°C water baths then tested for SBS in a universal testing machine (1 mm/minute). Kolmogorov-Smirnov and Levene tests were used to evaluate the distribution of the variable and the equality of variances respectively and a Student’s T- test was applied to compare the mean strength between the groups. In the next test, thirty disc shaped specimens were fabricated using Activa BioActive restorative and Equia Forte; 15 specimens from each material. The specimens of each group were immersed separately in 5 ml of deionized water. Fluoride release was measured daily throughout 15 days using a fluoride-specific ion electrode and an ion-analyzer. Repeated measures analysis of variance with one within-subject factor (time) and one between-subject factor (Activa Bioactive / Equia Forte) was applied to compare the amount of released fluoride between groups and within time. It was followed by univariate analyses and Bonferroni multiple comparisons tests. Results The mean shear bond strength of Activa Bioactive Restorative with adhesive was found to be 17.379 (± 8.5043) MPa and 19.443(± 8.3293) MPa for the Filtek Z350 XT/Z350 group. There was no significant difference between both groups. Regarding fluoride release, the amount of Fluoride released was significantly greater in the Equia Forte group compared to the Activa Bioactive group (- p-value <0.05). The mean amount of Fluoride has significantly decreased over time with Activa Bioactive group (- p-value <0.001); it showed the highest fluoride release during the first 24 hours post-setting. Also in the Equia Forte group, the mean amount of Fluoride release showed a progressive and significant decrease over time (- p-value <0.001), although the amount of Fluoride released was significantly greater in the Equia Forte group compared to the Activa Bioactive group (- p-value <0.05). Conclusions Activa Bioactive Restorative with adhesive and ...
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.