This paper describes the study of crack propagation and mechanical fracture in GaAs-on-Si, which are closely related with the residual stress. The crack propagation is often observed as the GaAs thickness exceeds about 3 µm, and the upper limit of the number of cracks increases linearly as the GaAs thickness increases. The cracks propagate from the surface defects, where stress ten times larger than the original residual thermal stress in GaAs-on-Si exists. The mechanical fracture strength (ζ) of the GaAs-on-Si wafer decreases as the GaAs thickness increases, and becomes equal to that of the bulk GaAs at the thickness of about 3 µm due to the concentrated stress near the cracks. The back coating of SiO2 is effective for stress relaxation, and the preliminary result of about 3×108 dyn/cm2 of stress relaxation is obtained.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.