The correlation between interfacial reactions and mechanical strengths of Sn(Cu)/Ni(P) solder bumps has been studied. Upon solid-state aging, a diffusioncontrolled process was observed for the interfacial Ni-Sn compound formation of the Sn/Ni(P) reaction couple and the activation energy is calculated to be 42 KJ/mol. For the Sn0.7Cu/Ni(P), in the initial aging, a needle-shaped Ni-Sn compound layer formed on Ni(P). Then, it was gradually covered by a layer of the Cu-Sn compound in the later aging process. Hence, a mixture layer of Ni-Sn and Cu-Sn compounds formed at the interface. For the Sn3.0Cu/Ni(P), a thick Cu-Sn compound layer quickly formed on Ni(P), which retarded the Ni-Sn compound formation and resulted in a distinct Cu-Sn compound/Ni(P) interface. The shear test results show that the mixture interface of Sn0.7Cu bumps have fair shear strengths against the aging process. In contrast, the distinct Cu-Sn/Ni(P) interface of Sn3.0Cu solder bumps is relatively weak and exhibits poor resistance against the aging process. Upon the reflowing process, the gap formation at the Ni(P)/Cu interface caused a fast degradation in the interfacial strength for Sn solder bumps. For Sn0.7Cu and Sn3.0Cu solder bumps, Ni 3 P formation was greatly retarded by the self-formed Cu-Sn compound layer. Therefore, Sn(Cu) solder bumps show better shear strengths over the Sn solder bump.
Sn whisker formation on Sn(Cu) finishes has been studied. (1) With respect to the thickness effect, we found that Sn whisker density for pure Sn and Sn0.7Cu finishes has a linear relationship with the finish thickness. The safety thickness for Sn and Sn0.7Cu finishes is about 10 mm and 20 mm, respectively. (2) With respect to the alloying effect, we found that Sn whisker formation could be retarded by increasing Cu content in the Sn(Cu) finishes. We conclude that the Cu additives could reduce the two major driving forces of the Sn whisker formation, i.e., metal underlayer dissolution and thermal stress. The Cu additives self-formed a Cu-Sn compound barrier layer, which effectively prevents the reaction and dissolution with the metal underlayer. On the other hand, the Cu additives precipitated out as Cu-Sn compound in the Sn(Cu) finish layer, which is believed to be the reason for smaller values of the coefficient of thermal expansion (CTE) for Sn(Cu) alloys. The smaller CTE values results in a lower thermal stress level in the Sn(Cu) finishes.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.