In general, mixed cations and anions containing formamidinium (FA), methylammonium (MA), caesium, iodine, and bromine ions are used to stabilize the black α-phase of the FA-based lead triiodide (FAPbI3) in perovskite solar cells. However, additives such as MA, caesium, and bromine widen its bandgap and reduce the thermal stability. We stabilized the α-FAPbI3 phase by doping with methylenediammonium dichloride (MDACl2) and achieved a certified short-circuit current density of between 26.1 and 26.7 milliamperes per square centimeter. With certified power conversion efficiencies (PCEs) of 23.7%, more than 90% of the initial efficiency was maintained after 600 hours of operation with maximum power point tracking under full sunlight illumination in ambient conditions including ultraviolet light. Unencapsulated devices retained more than 90% of their initial PCE even after annealing for 20 hours at 150°C in air and exhibited superior thermal and humidity stability over a control device in which FAPbI3 was stabilized by MAPbBr3.
High-efficiency lead halide perovskite solar cells (PSCs) have been fabricated with α-phase formamidinium lead iodide (FAPbI3) stabilized with multiple cations. The alloyed cations greatly affect the bandgap, carrier dynamics, and stability, as well as lattice strain that creates unwanted carrier trap sites. We substituted cesium (Cs) and methylenediammonium (MDA) cations in FA sites of FAPbI3 and found that 0.03 mol fraction of both MDA and Cs cations lowered lattice strain, which increased carrier lifetime and reduced Urbach energy and defect concentration. The best-performing PSC exhibited power conversion efficiency >25% under 100 milliwatt per square centimeter AM 1.5G illumination (24.4% certified efficiency). Unencapsulated devices maintained >80% of their initial efficiency after 1300 hours in the dark at 85°C.
The perovskite precursor solution chemistry is of paramount importance for well-controlled nucleation/crystal growth in solution-processed perovskite solar cells.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.