Low Ni-Cr-Mo alloys is developed by thermomechanical process to obtain high strength, toughness, and great hardenability properties. the aim of this study is to determine the correlation between the microstructure and corrosion properties after hot forging and followed by intercritical heating with cooling rate variation. Low Ni-Cr-Mo steel was homogenized, hot forgings at 950℃, and heat treated at 880℃ with three cooling variations by water, oil, and air. Intercritical heating makes a dual-phase structure. Metallorgaphy and hardness test is confirmed a mechanical properties. OCP and cyclic polarization test is confirmed a corrosion behavior. As the fast-cooling (water quenchant) show the lath martensite, bainite, and a few of acicular ferrite. The hardness of the 75-ton result is slightly lower than the 50-ton load, is reached 591±9.4 VHN for 75-ton and 597±15.6 VHN for 50-ton. Polarization test resulted corrosion resistance sample with 100 ton forging water quench has a high corrosion rate 0.8 mpy, higher than air quench 0.01 mpy.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.