This work reports the development of ultralight interwoven ultrathin graphitic carbon nitride (g-CN) nanosheets for use as a potential adsorbent in a passive sampler (PAS) designed to bind Hg2+ ions. The g-CN nanosheets were prepared from bulk g-CN synthesised via a modified high-temperature short-time (HTST) polycondensation process. The crystal structure, surface functional groups, and morphology of the g-CN nanosheets were characterised using a battery of instruments. The results confirmed that the as-synthesized product is composed of few-layered nanosheets. The adsorption efficiency of g-CN for binding Hg2+ (100 ng mL−1) in sea, river, rain, and Milli-Q quality water was 89%, 93%, 97%, and 100%, respectively, at natural pH. Interference studies found that the cations tested (Co2+, Ca2+, Zn2+, Fe2+, Mn2+, Ni2+, Bi3+, Na+, and K+) had no significant effect on the adsorption efficiency of Hg2+. Different parameters were optimised to improve the performance of g-CN such as pH, contact time, and amount of adsorbent. Optimum conditions were pH 7, 120 min incubation time and 10 mg of nanosheets. The yield of nanosheets was 72.5%, which is higher compared to other polycondensation processes using different monomers. The g-CN sheets could also be regenerated up to eight times with only a 20% loss in binding efficiency. Overall, nano-knitted g-CN is a promising low-cost green adsorbent for use in passive samplers or as a transducing material in sensor applications.

Studies of the production of fiber-forming polyamide 6 (PA6)/graphene composite material and melt-spun textile fibers are scarce, but research to date reveals that achieving the high dispersion state of graphene is the main challenge to nanocomposite production. Considering the significant progress made in the industrial mass production of graphene nanoplatelets (GnPs), this study explored the feasibility of production of PA6/GnPs composite fibers using the commercially available few-layer GnPs. To this aim, the GnPs were pre-dispersed in molten ε-caprolactam at concentrations equal to 1 and 2 wt %, and incorporated into the PA6 matrix by the in situ water-catalyzed ring-opening polymerization of ε-caprolactam, which was followed by melt spinning. The results showed that the incorporated GnPs did not markedly influence the melting temperature of PA6 but affected the crystallization temperature, fiber bulk structure, crystallinity, and mechanical properties. Furthermore, GnPs increased the PA6 complex viscosity, which resulted in the need to adjust the parameters of melt spinning to enable continuous filament production. Although the incorporation of GnPs did not provide a reinforcing effect of PA6 fibers and reduced fiber tensile properties, the thermal stability of the PA6 fiber increased. The increased melt viscosity and graphene anti-dripping properties postponed melt dripping in the vertical flame spread test, which consequently prolonged burning within the samples.

No abstract

No abstract