Tissue engineering offers a promising solution to the replacement of anterior cruciate ligament. A decellularized porcine patella tendon scaffold was produced by immersing whole tissues sequentially in hypotonic buffer, 0.1% (w/v) sodium dodecyl sulfate (SDS) in hypotonic buffer, and nuclease solution prior to sterilization with 0.1% (w/v) peracetic acid. Initial studies revealed that primary human tenocytes would attach to, but failed to penetrate into, the decellularized scaffold. A novel use of ultrasonication was therefore developed to allow extrinsic cells to migrate into the acellular scaffold. Various intensities of ultrasonication were tested in order to produce a microscopically more open porous matrix without damaging the overall architecture of the scaffold. Ultrasonication treatment with the intensity of 360 W and a pulse time of 1 s for a total of 1 min was found to be the optimal treatment. This process did not have a significant effect upon the biochemical constituents (collagen, glycosaminoglycans), nor did it denature the collagen. Moreover, the acellular sonicated scaffold retained the essential biomechanical characteristics of the native tissue. Primary human tenocytes penetrated into the center of whole acellular sonicated scaffolds over a 3-week period in static culture. The viability of the cells in the center of the scaffold (depth of circa 2.5 mm) was, however, compromised. To circumvent the problem of nutrient limitation, acellular sonicated scaffolds were split into fascicular scaffolds (500 mum thick). Cells seeded onto the fascicular scaffolds penetrated throughout the scaffold and remained viable after 3 weeks of culture. This study has shown that an acellular biocompatible tendon scaffold can be produced using 0.1% (w/v) SDS and that ultrasonication can provide a novel method to enhance the recellularization of decellularized natural tissues.
UHMWPE wear particles have been implicated in osteolysis, implant loosening, and long-term failure of total hip arthroplasties in vivo. This study examined four carbon-based composite materials as alternatives for UHMWPE in joint bearings. These materials were HMU-CVD, SMS-CVD, P25-CVD, and CFR-PEEK. New bearing materials should satisfy certain criteria: they should have good wear properties that at least match UHMWPE, and produce wear particles with low levels of biological activity. Of the four materials tested in multidirectional pin-on-plate tribological tests, SMS-CVD, P25-CVD, and CFR-PEEK showed lower volumetric wear factors than UHMWPE. P25-CVD had the lowest wear factor of 0.54 +/- 0.34 x 10(-7) mm(3)/Nm. Analysis of P25-CVD wear particles by transmission electron microscopy showed that the debris was very small, with the vast majority of particles being under 100 nm in size, which was similar in size to metal wear particles. The P25-CVD particles were isolated and cultured with L929 fibroblasts and U937 monocytic cells to assess their effect on cell viability. P25-CVD particles were significantly less cytotoxic (p < 0.01, ANOVA) to both cell types than CoCr metal wear particles. This work suggests that carbon-carbon composite materials may have potential for use in total hip replacement bearings. Of the materials tested P25-CVD had the lowest wear factor, and produced very small wear debris that had minimal cytotoxic effect on L929 and U937 cells in vitro. Therefore carbon-carbon composites, such as P25-CVD, may be important in the development of next-generation implants with lower wear rates and reduced cytotoxic potential.
Pyrophosphate ions are both inhibitors of HA formation and substrates for phosphatase enzymes. Unlike polyphosphates their hydrolysis results simultaneously in the complete loss of mineral formation inhibition and a localised elevation in orthophosphate ion concentration. Despite recent advances in our knowledge of the role of the pyrophosphate ion, very little is known about the effects of pyrophosphate on bone formation and even less is known about its local delivery. In this work we first developed a self setting pyrophosphate based calcium cement system with appropriate handling properties and then compared its in vivo degradation properties with those of a non-pyrophosphate containing control. Contrary to expectation, the presence of the pyrophosphate phase in the cement matrix did not inhibit mineralisation of the healing bone around the implant, but actually appeared to stimulate it. In vitro evidence suggested that enzymatic action accelerated dissolution of the inorganic pyrophosphate ions, causing a simultaneous loss of their mineralisation inhibition and a localised rise in supersaturation with respect to HA. This is thought to be a rare example of a biologically responsive inorganic material and these materials seem to be worthy of further investigation. Bioceramics to date have mainly been limited to orthophosphate, silicate and carbonate salts of calcium, here we report the successful application of a pyrophosphate material as a degradable osteoconductive bone repair cement.
This study isolated and characterized UHMWPE particles from 3 explant groups: early Charnley hip failures (ECE; < 10 years), late Charnley hip failures (LCE; > 10 years) and early knee failures (EKE; < 10 years). Debris isolated from the 3 groups had percentage particle number and percentage volumetric concentration distributions that were not significantly different. The greatest number of particles were found in the 0.1-0.5 microm size range and 19-20.6% of the volumetric concentration was below 1 microm in size in all groups. However, there were significant differences in the total volumetric concentration of debris isolated per g of tissue. LCE had significantly higher volumes of debris than ECE and EKE, there was no significant difference in the volume of debris from the EKE and ECE. The mean aspect ratio and mean irregularity ratio of the LCE group were also significantly higher than the ECE and EKE, suggesting that different wear mechanisms were occurring in the late Charnley group compared to the early Charnley and knee groups. These results also suggest that early knees, with normal surface wear, may have similar wear mechanisms to early Charnley hips and indicate that similar volumes of biologically active micrometer and sub-micrometer UHMWPE particles were produced. This may have important implications in the longer-term outcome of total knee arthroplasties, because it indicates a similar potential for osteolysis induced by wear debris.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.