A major limitation of the commonly used clinical MRI contrast agents (CAs) suitable at lower magnetic field strengths (<3.0 T) is their inefficiency at higher fields (>7 T), where next-generation MRI scanners are going. We present dysprosium nanoparticles (β-NaDyF4 NPs) as T2 CAs suitable at ultrahigh fields (9.4 T). These NPs effectively enhance T2 contrast at 9.4 T, which is 10-fold higher than the clinically used T2 CA (Resovist). Evaluation of the relaxivities at 3 and 9.4 T show that the T2 contrast enhances with an increase in NP size and field strength. Specifically, the transverse relaxivity (r2) values at 9.4 T were ∼64 times higher per NP (20.3 nm) and ∼6 times higher per Dy(3+) ion compared to that at 3 T, which is attributed to the Curie spin relaxation mechanism. These results and confirming phantom MR images demonstrate their effectiveness as T2 CAs in ultrahigh field MRIs.
X-ray luminescent nanoparticles (NPs), including lanthanide fluorides, have been evaluated for application to deep tissue in vivo molecular imaging using optical tomography. A combination of high material density, higher atomic number and efficient NIR luminescence from compatible lanthanide dopant ions indicates that particles that consist of ALnF4 (A = alkaline, Ln = lanthanide element) may offer a very attractive class of materials for high resolution, deep tissue imaging with X-ray excitation. NaGdF4:Eu3+ NPs produced an X-ray excited luminescence that was among the most efficient of nanomaterials that have been studied thus far. We have systematically studied factors such as (a) the crystal structure that changes the lattice environment of the doped Eu3+ ions within the unit cell; and extrinsic factors such as (b) a gold coating (with attendant biocompatibility) that couples to a plasmonic excitation, and (c) changes in the NPs surface properties via changes in the pH of the suspending medium—all with a significant impact on the X-ray excited luminescence of NaGdF4:Eu3+NPs. The luminescence from an optimally doped hexagonal phase NaGdF4:Eu3+ nanoparticle was 25% more intense compared to that of a cubic structure. We observed evidence of plasmonic reabsorption of midwavelength emission by a gold coating on hexagonal NaGdF4:Eu3+ NPs; fortunately, the NaGdF4:Eu3+ @Au core–shell NPs retained the efficient 5D0→7F4 NIR (692 nm) luminescence. The NaGdF4:Eu3+ NPs exhibited sensitivity to the ambient pH when excited by X-rays, an effect not seen with UV excitation. The sensitivity to the local environment can be understood in terms of the sensitivity of the excitons that are generated by the high energy X-rays (and not by UV photons) to crystal structure and to the surface state of the particles.
The synthesis and characterization of various rare-earth (RE)-doped and codoped yttrium oxide (Y2O3) nanomaterials were undertaken in the current work. RE dopants such as terbium (Tb), europium (Eu), and erbium (Er) were successfully doped, and ytterbium (Yb)−Er was codoped into Y2O3 nanomaterials. The as-synthesized nanomaterials are highly dispersed in the organic phase. X-ray diffraction peaks can be assigned to cubic Y2O3, which confirms the crystallinity of the as-prepared Y2O3 samples. Room temperature photoluminescence (PL) spectra showed characteristic emission peaks of Tb-, Eu-, and Er-doped Y2O3 samples. Up-conversion spectra of green and red emissions were also shown for Er−Yb-codoped Y2O3 samples. It was found that the intensities of the green and red emissions could be altered by varying the dopant concentration. The nanocrystals were surface-functionalized with an amine (NH2) group via a reverse microemulsion method. The amine groups render the nanocrystals water-soluble and also afford them with the possibility of further functionalization by other biomolecules. in vitro cytotoxicity studies showed that the synthesized nanocrystals have no appreciable toxicity on human hepatocellular carcinoma (Hep-G2) cells at concentrations of 0.007−0.063 mg/mL. Because of the Y2O3:RE nanomaterials’ well-dispersity in water, low toxicity, and good PL, they can potentially be used as fluorophores in bioimaging.
The deposition, clearance and translocation of europium-doped gadolinium oxide nanoparticles in a mouse lung were investigated experimentally. Nanoparticles were synthesized by spray flame pyrolysis. The particle size, crystallinity and surface properties were characterized. Following instillation, the concentrations of particles in organs were determined with inductively coupled plasma mass spectrometry. The protein corona coating the nanoparticles was found to be similar to the coating on more environmentally relevant nanoparticles such as iron oxide. Measurements of the solubility of the nanoparticles in surrogates of biological fluids indicated very little propensity for dissolution, and the elemental ratio of particle constituents did not change, adding further support to the contention that intact nanoparticles were measured. The particles were intratracheally instilled into the mouse lung. After 24 hours, the target organs were harvested, acid digested and the nanoparticle mass in each organ was measured by inductively coupled plasma mass spectrometry (ICP-MS). The nanoparticles were detected in all the studied organs at low ppb levels; 59% of the particles remained in the lung. A significant amount of particles was also detected in the feces, suggesting fast clearance mechanisms. The nanoparticle system used in this work is highly suitable for quantitatively determining deposition, transport and clearance of nanoparticles from the lung, providing a quantified measure of delivered dose.
The growing use of silver nanoparticles (AgNPs) in consumer products raises concerns about potential health effects. This study investigated the persistence and clearance of 2 different size AgNPs (20 and 110 nm) delivered to rats by single nose-only aerosol exposures (6 h) of 7.2 and 5.4 mg/m(3), respectively. Rat lung tissue was assessed for silver accumulations using inductively-coupled plasma mass spectrometry (ICP-MS), autometallography, and enhanced dark field microscopy. Involvement of tissue macrophages was assessed by scoring of silver staining in bronchoalveolar lavage fluid (BALF). Silver was abundant in most macrophages at 1 day post-exposure. The group exposed to 20 nm AgNP had the greatest number of silver positive BALF macrophages at 56 days post-exposure. While there was a significant decrease in the amount of silver in lung tissue at 56 days post-exposure compared with 1 day following exposure, at least 33% of the initial delivered dose was still present for both AgNPs. Regardless of particle size, silver was predominantly localized within the terminal bronchial/alveolar duct junction region of the lung associated with extracellular matrix and within epithelial cells. Inhalation of both 20 and 110 nm AgNPs resulted in a persistence of silver in the lung at 56 days post-exposure and local deposition as well as accumulation of silver at the terminal bronchiole alveolar duct junction. Further the smaller particles, 20 nm AgNP, produced a greater silver burden in BALF macrophages as well as greater persistence of silver positive macrophages at later timepoints (21 and 56 days).
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.