Background and Objectives:Endodontic sealer is currently regarded with such importance in the root canal treatment that it is often considered to be more important than the core obturating material itself. Sealer with the least film thickness is favorable for minimizing microleakage. The aim of the study is to compare sealer distribution in root canal using three different sealers with three different obturation techniques.Materials and Methods:AH plus, Fuji-1, Tubliseal Extended Working Time (EWT) was placed into the prepared root canals of 90 maxillary central incisors using a lentulospiral. Thereafter, the canals were obturated using three different gutta-percha root filling techniques (single cone, lateral condensation, vertical condensation). Horizontal sectioning was carried out at 3 mm and 6 mm from the apex with a diamond disk. The two specimens thus obtained were examined for sealer distribution using a stereomicroscope and the percentage of sealer coating the perimeter (PSCP) was calculated using a digital imaging system.Results:A significant difference existed in the mean PSCP values of three different sealers (P < 0.000), where Tubliseal (EWT) had the highest PSCP values followed by the AH plus and Fuji-1. Also, between techniques, differences were observed (P < 0.00), where a single cone technique had the highest mean values followed by lateral condensation and vertical condensation. Between the 3 mm and 6 mm sections a non-significant difference was observed (P < 0.945).Conclusion:Tubliseal EWT showed highest PSCP value and Single cone technique showed the higher PSCP value then lateral and vertical condensation technique at 3 mm and 6 mm sections.
Introduction: Coronal leakage is one of the constant concerns in routine dental practice. It is one of the factors responsible for the failure of root canal therapy. Permanent restorations should be given as soon as possible after the completion of root canal therapy. If unavoidable, provisional restoration should be given in such a way that it maximally reduced the leakage of micro organisms and fluids from the external environment into the canal space. Hence, we evaluated the effect of saliva on the coronal leakage of temporary restorations.
Materials and methods:Biomechanical preparation of the root canals of 204 fresh mandibular first premolar teeth was done using endodontic files with intermittent irrigation of sodium hypochlorite solution and ethylenediaminetetraacetic acid. Alternate irrigation with normal saline was done periodi cally. After preparation, drying of the canals was done using paper points followed by sealing of the apical foramen. For the assessment of the microleakage, Siqueira et al apparatus and method was used. All the specimens were divided into four groups based on the provisional restorative material used. All the groups were further divided into three subgroups based on the presence and absence of intracanal medicaments. Verissimo et al's criteria were used to check the turbidity at 1, 2, 3, and 4week interval respectively. All the results were analyzed by
Aim and Objectives:Acrylic teeth are used for fabrication of dentures. Debonding of tooth – denture base bond is routine problem in dental practice. The aim of this study was to comparatively evaluate failure load of acrylic resin denture teeth bonded to three different heat resin.Materials and Methods:Four groups were created out of test samples central incisors (11). Group I: Control, whereas Group II, Group III and Group IV were experimental groups modified with diatoric hole, cingulum ledge lock and Teeth modified with both diatoric hole and cingulum ledge lock, respectively. These test specimens with 3 teeth (2 central [11, 21] and 1, lateral [12] incisors) positioned imitating arrangement of teeth in the conventional denture, prepared by three different heat cure materials (DPI, Trevalon, Acralyn-H). A shear load was applied at cingulum of central incisor (11) at 130° to its long axis using universal tester at a cross head speed of 5 mm/min until failure occurred. Failure load test was conducted and statistical analysis was performed using SPSS 16 software package (IBM Company, New York, U.S).Results:Highest failure load was seen in Group IV specimens, prepared by Trevalon but did not significantly differ from that of DPI.Conclusion:The failure load of bonding denture teeth to three different heat cure materials was notably affected by modifications of ridge lap before processing. The specimens with a combination of diatoric hole and cingulum ledge lock, prepared by Trevalon showed highest failure load but did not significantly vary from that of DPI. The control group prepared by Acralyn-H showed lowest failure load but did not significantly differ from that of DPI.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.