The inhibition effect of gum arabic (GA) was investigated using weight loss measurements and electrochemical techniques. The results show that the inhibition efficiency of GA increased with an increase in the concentration of the inhibitor but decreased with the temperature. Immersion time was found to have a profound effect on the corrosion inhibition performance of the inhibitor. Polarization measurements revealed that GA was a mixed-type inhibitor, with higher influence on the anodic reaction. The inhibitor followed the Temkin’s adsorption isotherm, and the values of the standard free adsorption energy indicate a mixed-type adsorption, with the physical adsorption being more dominant. SEM–EDS and FT-IR measurements were also employed to support the findings.
Guar gum (GG) was investigated as a possible eco-friendly corrosion inhibitor for pure aluminium in a 1-M HCl solution at different temperatures and immersion times using gravimetric and electrochemical techniques. The results showed that GG was a good corrosion inhibitor for pure aluminium in the studied environment. The inhibition efficiency of GG increased with increasing inhibitor concentration and immersion time but decreased with increasing temperature. Polarisation measurements revealed that GG was a mixed type inhibitor with a higher influence on the cathodic reaction. The adsorption behaviour of the investigated inhibitor was found to obey the Temkin adsorption isotherm and the calculated values of the standard free adsorption energy indicate mixed-type adsorption, with the physical adsorption being more dominant. The associated activation energy (Ea) and the heat of adsorption (Qa) supported the physical adsorption nature of the inhibitor. Fourier-transform infrared spectroscopy (FTIR) and Raman/SERS were used to explain the adsorption interaction between the inhibitor with the surface of the metal. The results suggested that most inhibition action of GG is due to its adsorption of the metal surface via H-bond formation.
The effect of CO2 partial pressure on the corrosion inhibition efficiency of gum arabic (GA) on the N80 carbon steel pipeline in a CO2-water saline environment was studied by using gravimetric and electrochemical measurements at different CO2 partial pressures (e.g., PCO2 = 1, 20 and 40 bar) and temperatures (e.g., 25 and 60 °C). The results showed that the inhibitor efficiency increased with an increase in inhibitor concentration and CO2 partial pressure. The corrosion inhibition efficiency was found to be 84.53% and 75.41% after 24 and 168 h of immersion at PCO2 = 40 bar, respectively. The surface was further evaluated by scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), grazing incidence X-ray diffraction (GIXRD), and X-ray photoelectron spectroscopy (XPS) measurements. The SEM-EDS and GIXRD measurements reveal that the surface of the metal was found to be strongly affected by the presence of the inhibitor and CO2 partial pressure. In the presence of GA, the protective layer on the metal surface becomes more compact with increasing the CO2 partial pressure. The XPS measurements provided direct evidence of the adsorption of GA molecules on the carbon steel surface and corroborated the gravimetric results.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.