The object of the work has been to investigate experimentally the mechanisms of erosion in metals and alloys under drop impingement attack. For this purpose an apparatus of the wheel and jet type has been used to erode aluminium, copper, iron, cobalt and alloys of these metals. The various stages in the process from the first detectable microplastic deformation to the eventual pitting and removal of material from the surface have been investigated. In addition, experiments were carried out with the purpose of examining the effects of the normal impact pressure of a liquid on a surface in the absence of shear forces associated with liquid flow. This was achieved by propagating impact-generated compression waves through a liquid column in a filled and sealed cylinder onto a specimen surface inside the cylinder. With this arrangement the initial damage—small shallow depressions in the specimen surface— was identical with that produced under standard drop impact conditions in the wheel and jet apparatus. In either case the calculated values of the maximum impact pressure were lower than the average yield strength of each metal investigated. A complementary series of experiments was carried out in order to examine the erosive effects of liquid flow over the surface in the absence of high impact pressures. The technique used here involved a continuous high-speed water jet impinging against a solid surface at glancing incidence. This study showed that while flat well polished surfaces were apparently unaffected by the flow, lightly roughened surfaces or surfaces which contained the shallow impact depressions were severely eroded in regions adjacent to discontinuities. These various experiments suggest that the initial yielding which gives rise to the depression is associated with non-uniformity in the strength, structure and shape of the solid surface rather than with local variations in the impact pressure over the surface. The subsequent acceleration in the erosion rate is linked with the increased roughening of the surface and with an increase in the shear damage. When the surface becomes very rough and pitted, the impinging drop is deflected into less damaging streams by surface projections. This effect would account for the eventual decrease observed in the erosion rate. Further studies of the structure of the eroded surfaces have shown that the fractures have a number of features which are characteristic of metal fatigue failure. The connexion between erosion and fatigue is illustrated by similarities between the endurance curves for erosion and for the same metal in a standard fatigue test. As in the case of fatigue failure, strain energy to fracture appears to be one of the most important mechanical properties determining the erosive behaviour of a ductile metal.
Experiments have been carried out to investigate the initial stages in the deformation of metals due to repeated liquid impacts. The initiation of damage is discussed and a comparison made with the initial stages of deformation in metals subjected to similar hydrodynamic loading conditions due to the action of shock waves in a liquid. The destructive role played by the rapid flow of liquid across the surface of a specimen after impact is also described.
This report was prepBred aa an accoont of Gavenunent sponsored work. Neither the United States, nor the Commission, nor any person acting on behslf of the Commission: A. Makes any warranty or representaticm. expressed or implied, witb respect to tbe accuracy, completeness, or uee&iln«SB of ti^ Inibrmation contained In this report, or that the use of any information, spfiaratus. method, or process disclosed in this report may not infringe privately owned ri^ts; or B. Assumes any liabilities willi respect to the use of, or for damages resulting from the use of any information, appMratos, method, or process disclosed In this report. Aa used in the above, "perMo acUog OD behalf of the Commission" Includes any employee or contractor of the CommissiMi, or emfdoyee of such contractor, to the extent that such employee or c
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.