Transmission electron microscopy has been applied to characterize the structure of Ti/Al and Ti/Al/Ni/Au Ohmic contacts on n-type GaN (∼1017 cm−3) epitaxial layers. The metals were deposited either by conventional electron-beam or thermal evaporation techniques, and then thermally annealed at 900 °C for 30 s in a N2 atmosphere. Before metal deposition, the GaN surface was treated by reactive ion etching. A thin polycrystalline cubic TiN layer epitaxially matched to the (0001) GaN surface was detected at the interface with the GaN substrate. This layer was studied in detail by electron diffraction and high resolution electron microscopy. The orientation relationship between the cubic TiN and the GaN was found to be: {111}TiN//{00.1}GaN, [110]TiN//[11.0]GaN, [112]TiN//[10.0]GaN. The formation of this cubic TiN layer results in an excess of N vacancies in the GaN close to the interface which is considered to be the reason for the low resistance of the contact.
Transmission electron microscopy, x-ray diffraction, low-temperature photoluminescence, and Raman spectroscopy were applied to study stress relaxation and the dislocation structure in a Si-doped GaN layer in comparison with an undoped layer grown under the same conditions by metalorganic vapor phase epitaxy on (11.0) Al2O3. Doping of the GaN by Si to a concentration of 3×1018 cm−3 was found to improve the layer quality. It decreases dislocation density from 5×109 (undoped layer) to 7×108 cm−2 and changes the dislocation arrangement toward a more random distribution. Both samples were shown to be under biaxial compressive stress which was slightly higher in the undoped layer. The stress results in a blue shift of the emission energy and E2 phonon peaks in the photoluminescence and Raman spectra. Thermal stress was partly relaxed by bending of threading dislocations into the basal plane. This leads to the formation of a three-dimensional dislocation network and a strain gradient along the c axis of the layer.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.