Future applications of ultrafine-grained, high performance materials produced by equalchannel angular pressing (ECAP) will most likely require processing on an industrial scale. There is a need for detailed microstructural and mechanical characterisation of large-scale, ECAP-processed billets. In the present study, we examine the microstructure and mechanical properties as a function of location and orientation within large (50 x 50 x 300 mm³) billets of an Al-6060 alloy produced by ECAP (90° channel angle) with different magnitudes of backpressure. The internal deformation is analysed using a grid-line method on split billets. Hardness is recorded in longitudinal and crosssectional planes. In order to further characterise the local, post-ECAP mechanical properties, tensile tests in different layers are performed. Moreover, low-voltage scanning transmission electron microscopy observations highlight relevant microstructural features. We find that the homogeneity and anisotropy of mechanical properties within the billets depend significantly on the geometry of the shear zone. We demonstrate that deformation gradients can be reduced considerably by increasing the backpressure: The opening-angle of the fan-shaped shear zone is reduced from ψ ≈ 20 ° to ψ ≈ 7 ° when the backpressure is increased from 0 to 150 MPa. Backpressures of 150 MPa result in excellent homogeneity, with a relative variation of tensile mechanical properties of less than 7 %. Our investigation demonstrates that ECAP is suitable for processing homogenous, high performance materials on a large scale, paving the way for advanced industrial applications.
Different modes of introduction of yttrium have been tested with regard to the influence on the high temperature oxidation behavior of a FeCral alloy. Y2O3 sol‐gel coatings, Y2O3 metal‐organic chemical vapor deposition (MOCVD) coatings, implanted yttrium ions and yttrium as alloying element (0.1 wt.%) in the same Fe‐20Cr‐5Al alloy were oxidized at 1100°C in air under atmospheric pressure. Whatever the mode of introduction of the reactive element, the oxidation rates were not decreased compared to the oxidation rate of the blank specimen. The observation of the oxidized surface indicated that the alumina scale largely spalled from the blank alloy. Spallation was reduced for the Y2O3 sol‐gel coated, the Y2O3 MOCVD coated alloys and the yttrium ion implanted steels. The Y‐containing alloy did not exhibit any detachment of the oxide scale, indicating the best high temperature oxidation behavior, at least from the viewpoint of scale adherence.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.