TheraCal displayed higher calcium-releasing ability and lower solubility than either ProRoot MTA or Dycal. The capability of TheraCal to be cured to a depth of 1.7 mm may avoid the risk of untimely dissolution. These properties offer major advantages in direct pulp-capping treatments.

calcium silicate-based cements are biointeractive (ion-releasing) bioactive (apatite-forming) functional biomaterials. The high rate of calcium release and the fast formation of apatite may well explain the role of calcium silicate biomaterials as scaffold to induce new dentin bridge formation and clinical healing.

Siboni F, Taddei P, Zamparini F, Prati C, Gandolfi MG. Properties of BioRoot RCS, a tricalcium silicate endodontic sealer modified with povidone and polycarboxylate.International Endodontic Journal, 50, e120-e136, 2017.Aim To evaluate the chemical and physical properties of a tricalcium silicate root canal sealer containing povidone and polycarboxylate (BioRoot RCS), a calcium silicate MTA-based sealer containing a salicylate resin (MTA Fillapex), a traditional eugenolcontaining sealer (Pulp Canal Sealer) and an epoxy resin-based root canal sealer (AH Plus). Methodology Calcium release, pH, setting time, water sorption, volume of open pores, volume of impervious portion, apparent porosity and weight loss were measured. The ability to nucleate calcium phosphates (CaP) after ageing 28 days in a simulated body fluid was evaluated using ESEM-EDX and microRaman spectroscopy. Data were statistically analysed (P = 0.05) using one-way ANOVA (setting time, radiopacity, solubility, water sorption, porosity) or two-way ANOVA (ion release tests). Results BioRoot RCS had a final setting time of 300 min and adequate radiopacity (5.2 mm Al). It demonstrated the highest (P < 0.05) and more prolonged ability to release calcium ions (721 ppm at 3 h) and to increase the pH (11-12) (P < 0.05); Btype carbonated apatite deposits were found on aged BioRoot RCS (biointeractivity-related CaP-forming ability). A final setting time of 270 min and good calcium release (17.4 ppm at 3 h) were measured for MTA Fillapex; apatite deposits were present on aged samples. No calcium release and no alkalizing activity were measured for Pulp Canal Sealer and AH Plus; no CaP nucleation was detected on aged Pulp Canal Sealer, and some apatite deposits were found on aged AH Plus (chemi/physisorption-related CaP-deposition). Higher and significantly different (P < 0.05) porosity, water sorption and solubility were measured for the two calcium silicate sealers, especially for BioRoot RCS. Conclusions BioRoot RCS had bioactivity with calcium release, strong alkalizing activity and apatiteforming ability, and adequate radiopacity.

No abstract

No abstract