a b s t r a c tNanocrystalline nickel ferrite (NiFe 2 O 4 ) has been synthesized from a stoichiometric mixture of oxides NiO and ␣-Fe 2 O 3 in a high energy planetary mill. An annealing at 350 • C, after milling, was used to improve the solid state reaction. The obtained powders were investigated by X-ray diffraction, magnetic measurements, scanning electron microscopy, X-ray microanalysis and differential scanning calorimetry. The particles size distribution was analyzed using a laser particle size analyser. The nickel ferrite begins to form after 4 h of milling and continuously form up to 16 h of milling. The obtained nickel ferrite has many inhomogeneities and a distorted spinel structure. The mean crystallites size at the final time of milling is 9 ± 2 nm and the lattice parameter increases with increase the milling time. DSC measurements revealed a large exothermic peak associated with cations reordering in the crystalline structure. The magnetization of the obtained powder depends on the milling time and annealing. After the complete reaction between the starting oxides the milling reduces the magnetization of the samples. The magnetization increases after annealing, due to the reorganization of the cations into the spinel structure.
Nano-lubricants offer improved tribological properties in many applications, such as machines and engines. The presence of nanoparticles in the lubricating oil affects its wear, friction, thermal, chemical and physical properties in many ways. Titanium dioxide (TiO2) is a promising lubricant additive for enhanced engine efficiency. This article reports the effect of 10 W-30 pure base engine oil suspended TiO2 nanoparticles. Four different volume concentrations (0.01%, 0.025%, 0.050% and 0.075%) of TiO2 nanoparticles in the base lubricating oil are used for the analysis. The tribological tests were performed at ambient temperature as well as at 75 °C using a four ball tribometer. Scanning electron microscope (SEM) and Alicona Inginite Focus G5 microscope were used to analyze the worn surface. The results show that the surface-modified TiO2 nanoparticles can remarkably improve the load-carrying capacity, the friction reducing, and anti-wear abilities of the additive oil. The diameter of the wear trace and the coefficient of friction are the tribological properties analyzed for the nano-lubricant prepared at different volume concentration (VC). It was found that the diameter of the wear scar and the coefficient of friction increase with increasing VC of TiO2 nanoparticles in the lubricating oil. The main objective of the paper is to present the recent progress and, consequently, to develop a comprehensive understanding of the tribological behavior of engine oil mixed with TiO2 nanoparticles.
In the present work, the inhibitive action of natural propolis on bronze corrosion in a weakly acidic solution containing Na2SO4 and NaHCO3 at pH 5 was evaluated using multiscale electrochemical techniques, namely potentiodynamic polarization, electrochemical impedance spectroscopy and scanning vibrating electrode technique measurements. The major constituents of propolis were identified by HPLC. Surface characterization was performed by SEM-EDX and AFM analysis. Experiments were performed as a function of the propolis concentration and immersion time in the corrosive electrolyte. The obtained results showed that propolis presents good anticorrosive properties on bronze, acting as a mixed-type inhibitor, but its protective effectiveness is time-dependent. The highest inhibiting efficiency of 98.9% was obtained in the presence of 100 ppm propolis, after about 12 h of exposure to inhibitor-containing electrolyte through the stabilization of Cu2O on the bronze surface. The inhibitive properties of propolis on bronze corrosion are likely due to the adsorption of its main constituents (flavonoids and phenolic compounds), through the oxygen atoms in their functional groups and aromatic rings, which have been evidenced by FT-IR spectra. The adsorption of propolis on bronze was found to follow Langmuir adsorption isotherm.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.