Polyetheretherketone (PEEK) composites exhibit high stiffness, chemical stability, and heat resistance and they are therefore employed in applications under severe operating environments. This work aims to provide insight into the effect of the size, concentration, and type of fillers on the thermal and mechanical properties of PEEK. A total of 32 composites are used to highlight the influence of nature (lamellae, such as boron nitride and graphite and silicon carbide and alumina), size (nano and micrometric), and content (2.5, 5, 7.5, and 10 vol%) of fillers. The melting temperature and lamellar thickness did not change regardless of the nature of the filler. The thermomechanical analysis demonstrates that lamellar fillers form a percolating network and contribute significantly to the enhancement of the storage modulus. The increase in the storage modulus is proportional to the filler content, and it is more pronounced for micro composites.As expected, the percolating network is formed at lower concentrations for lamellar fillers than for spherical ones. The highest conductivity is achieved with graphite at 0.823 W m À1 K À1 , which is twice that of PEEK for 10 vol%. Moreover, the use of micrometric fillers results in thermal conductivity enhancement attributed to the higher amount of efficient hot zones for heat transfer.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.