Objective: The purpose of this study was to evaluate the effect of the Yd:YAG laser irradiation on orthodontic bracket base surface. Shear bond strength (SBS) values and sites of the bonding failure interfaces were quantified. Methods: Brackets were divided into two groups: OP (One Piece - integral sandblast base) and OPL (One Piece - laser irradiation). The brackets were randomly bonded on an intact enamel surface of 40 bovine incisors. The SBS tests were carry out using a universal test machine. A stereomicroscopy was used to evaluate the adhesive remnant index (ARI), and surface characterization was performed by scanning electron microscopy (SEM). Student’s t-test was used to compare the SBS between the two groups (p< 0.05). Frequencies and chi-square analysis were applied to evaluate the ARI scores. Results: OPL group showed higher value (p< 0.001) of SBS than OP group (43.95 MPa and 34.81 MPa, respectively). ARI showed significant difference (p< 0.001) between OPL group (ARI 0 = 100%) and OP group (ARI 0 = 15%). SEM showed a higher affinity between the adhesive and the irradiated laser base surface. Conclusions: Yd:YAG laser irradiation on bracket base increased SBS values, showing that bonding failure occurs at the enamel/adhesive interface. Laser-etched bracket base may be used instead of conventional bases in cases where higher adhesion is required, reducing bracket-bonding failure.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.