Orthodontic treatment with fixed brackets plays a major role on the formation of white spot lesions. Objective This study aimed to incorporate silver nanoparticle solutions (AgNP) in an orthodontic adhesive and evaluate its physicochemical and antimicrobial properties.Material and Methods Silver nanoparticle solutions were added to a commercial adhesive in different concentrations (w/w): 0%, 0.11%, 0.18%, and 0.33%. Shear bond strength (SBS) test was performed after bonding metal brackets to enamel. Raman spectroscopy was used to analyze in situ the degree of conversion (DC) of the adhesive layer. The surface free energy (SFE) was evaluated after the measurement of contact angles. Growth inhibition of Streptococcus mutans in liquid and solid media was determined by colony-forming unit count and inhibition halo, respectively. One-way ANOVA was performed for SBS, DC, SFE, and growth inhibition.Results The incorporation of AgNP solution decreased the SBS (p<0.001) and DC in situ (p<0.001) values. SFE decreased after addition of 0.18% and 0.33% AgNP. Growth inhibition of S. mutans in liquid media was obtained after silver addition (p<0.05).Conclusions The addition of AgNP solutions to Transbond™ XT adhesive primer inhibited S. mutans growth. SBS, DC, and SFE values decreased after incorporation up to 0.33% AgNP solution without compromising the chemical and physical properties of the adhesive.
The use of adhesives containing triclosan-loaded halloysite represents a promising "smart" approach to bond orthodontic brackets and bands; these might prevent enamel demineralisation and induce enamel remineralisation during the treatment.
This study is aimed at evaluating the effects of triclosan-encapsulated halloysite nanotubes (HNT/TCN) on the physicochemical and microbiological properties of an experimental dental composite. A resin composite doped with HNT/TCN (8% w/w), a control resin composite without nanotubes (HNT/TCN-0%) and a commercial nanofilled resin (CN) were assessed for degree of conversion (DC), flexural strength (FS), flexural modulus (FM), polymerization stress (PS), dynamic thermomechanical (DMA) and thermogravimetric analysis (TGA). The antibacterial properties (M) were also evaluated using a 5-day biofilm assay (CFU/mL). Data was submitted to one-way ANOVA and Tukey tests. There was no significant statistical difference in DC, FM and RU between the tested composites (p > 0.05). The FS and CN values attained with the HNT/TCN composite were higher (p < 0.05) than those obtained with the HNT/TCN-0%. The DMA analysis showed significant differences in the TAN δ (p = 0.006) and Tg (p = 0) between the groups. TGA curves showed significant differences between the groups in terms of degradation (p = 0.046) and weight loss (p = 0.317). The addition of HNT/TCN induced higher PS, although no significant antimicrobial effect was observed (p = 0.977) between the groups for CFUs and (p = 0.557) dry weight. The incorporation of HNT/TCN showed improvements in physicochemical and mechanical properties of resin composites. Such material may represent an alternative choice for therapeutic restorative treatments, although no significance was found in terms of antibacterial properties. However, it is possible that current antibacterial tests, as the one used in this laboratory study, may not be totally appropriate for the evaluation of resin composites, unless accompanied with aging protocols (e.g., thermocycling and load cycling) that allow the release of therapeutic agents incorporated in such materials.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.