No abstract

Conductive and flexible bio-based materials consisting of chitosan films coated with conductive poly­(3-hexylthiophene) (P3HT) were prepared. Thermal, optical, mechanical, morphological, wettability, and conductive properties were analyzed. In a very simple and effective method of chitosan film modification, a controlled volume of a P3HT solution was deposited onto a previously formed chitosan film, assisted by the spin coating method. Later, P3HT-coated chitosan films were doped by simple contact with an aqueous solution of HAuCl4. The use of HAuCl4 becomes attractive because the reports on the doping process in this type of material using this reagent are still scarce and recent to date. In addition, since this acid is a well-known metal nanoparticle precursor, its use opens new future perspectives for these materials into new applications. The effect of P3HT concentration and doping times on film properties was studied. Attenuated total reflectance spectroscopy and UV–Vis spectroscopy allowed us to demonstrate that the presence of the P3HT coating and its doping induce significant changes in the vibrational modes and optoelectronic properties of samples. Additionally, the images obtained by scanning electron microscopy showed a well-distributed and homogeneous coating on the surface of chitosan films. Measured conductivity values of doped film samples fall in the range from 821.3 to 2017.4 S/m, representing, to the best of our knowledge, the highest values reported in the literature for chitosan/chitin-based materials. Indeed, these values are around or even higher than those obtained for some materials purely consisting of conductive polymers.

No abstract

Poly[(5,5’-(2,3-bis(2-ethylhexyloxy)naphthalene-1,4-diyl)bis(thiophene-2,2′-diyl))-alt-(2,1,3-benzothiadiazole-4,7-diyl)] (PEHONDTBT) was synthesized for the first time and through direct arylation polymerization (DAP) for use as p-donor material in organic solar cells. Optimized reaction protocol leads to a donor-acceptor conjugated polymer in good yield, with less structural defects than its analog obtained from Suzuki polycondensation, and with similar or even higher molecular weight than other previously reported polymers based on the 2,3-dialkoxynaphthalene monomer. The batch-to-batch repeatability of the optimized DAP conditions for the synthesis of PEHONDTBT was proved, showing the robustness of the synthetic strategy. The structure of PEHONDTBT was corroborated by NMR, exhibiting good solubility in common organic solvents, good film-forming ability, and thermal stability. PEHONDTBT film presented an absorption band centered at 498 nm, a band gap of 2.15 eV, and HOMO and LUMO energy levels of −5.31 eV and −3.17 eV, respectively. Theoretical calculations were performed to understand the regioselectivity in the synthesis of PEHONDTBT and to rationalize its optoelectronic properties. Bilayer heterojunction organic photovoltaic devices with PEHONDTBT as the donor layer were fabricated to test their photovoltaic performance, affording low power-conversion efficiency in the preliminary studies.

No abstract

No abstract

No abstract

No abstract