The concept of self-healing concrete is becoming more necessary as sustainability in construction is more desirable. Amongst the current solutions in this technology are autogenous, chemical, and bacterial self-healing. It is paramount that secondary raw materials be used in the production of selfhealing concrete as a form of a sustainable solution. Therefore, in this paper, the admixture “Betocrete-CP-360-WP”, which is a crystallizing waterproofing admixture with hydrophobic effect and is 100% recyclable, has been used and its effect on the physical, chemical, and mechanical properties of concrete, as well as selfhealing capabilities of concrete, have been determined. According to the obtained results, the crystalline additive “Betocrete-CP-360-WP” has no effect on density and slightly increases the amount of entrained air in the concrete mix. However, it does decrease the workability of the concrete mixture which could prove problematic in transportation to the construction site or in concreting in general. Also, with the crystalline admixture in the concrete mix, a 60% reduction in concrete compressive strength after one day of hardening has been estimated, but after 7 and 28 days, the strength attained is within the ranges of the control samples. In addition, concrete containing Betocrete-CP360-WP was 30% less water permeable as compared to control samples. The self-healing efficiency of the concrete was determined by a water flow test through a formed crack (approximately 0.35 mm wide). This was done by gluing a plastic pipe to the top of the cracked concrete specimens and maintaining a constant pressure of the water in the pipe. The experiment was continued for 28 days, and the crack self-healing efficiency of the concrete was calculated from the differences in the amount of water passed through the crack before healing and after 7, 14, 21 and 28 days of the healing process. After 28 days of the water flow test, the cracks in the concrete with the crystalline admixture and recycled concrete dust were completely healed, while the control specimens were not.
Concrete plants accumulate large amounts of concrete wash water. This water, which pH is highly alkaline, has a negative impact on the environment. Its reuse in fresh concrete slightly reduces its mechanical properties. The combination of concrete wash water and zeolitic by-product led to an increase of 4.6% in the compressive strength at 7 days hydration and up to 30% at 28 days hydration. The same combination led to the denser microstructure compared to the samples made with concrete wash water. This could be explained by the pozzolanic reaction of the zeolitic by-product. The complex chemical reactions of cement, zeolitic by-product, and fines presented in the concrete wash water occurred. Therefore, it was suggested the reusing method of concrete wash water together with zeolitic by-product in the fresh concrete mixtures by substituting some amount of tap water with concrete wash water. In this way, the consumption of tap water is possible to reduce in cement systems.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.