Commercial ceramics for dental computer aided design/computer aided manufacture (CAD/CAM) restorations suffer from surface chipping defects and microcracking. The influence of CAD/CAM machining of dental materials on the mechanical strength and extension of the damage zone was studied. Two different commercial dental ceramics, a feldspathic porcelain and a glass-ceramic, were CAD/CAM machined according to dental practice. The extension of the damage zone was analysed by a stepwise erosion of the surface, and the biaxial flexural strength was measured. To simulate the adhesive fixing of ceramic inlays, the specimens were sealed using a light-curing monomer. The different machining behaviour is dominated by the microstructure of the investigated materials. Owing to the high amount of glassy phase, the feldspathic porcelain shows extensive microcracking and chipping defects. The extent of the damage zone can be determined as 40-60 microm. Sealing of the surface did not affect the flexural strength of the machined samples. The dominating response to machining of the glass-ceramic is crushing and crumbling with a major contribution of plastic deformation on a microscopic scale. The extent of the damage zone is less than 20 microm. These cracks can be bridged by sealing of the surface, resulting in a substantial increase in strength.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.