SynopsisThe mechanical properties, tensile strength, and elongation were investigated for poly(viny1 chloride) (PVC) samples mixed with dioctylphthalate (DOP) at concentrations from 0 to 100 parts per hundred parts PVC at 23°C. It was found that the tensile strength decreased with the increase of concentration, and the elongation was increased until a concentration of 30 DOP content, and then decreased. This leads to the suggestion that intermolecular plasticization is dominant until 30 DOP content, while interstructural plasticization is prevailing for higher concentrations. The permittivity E' and the dielectric loss factor E" of the same samples have been measured in the frequency range 102-106 Hz at temperatures from 3 to 96°C. Results show that as the DOP content increases in PVC, the dielectric absorption becomes broader, and the glass transition temperature T, is lowered. The magnitude of the loss peak decreases with an increase of DOP content to a minimum at concentrations from 40 to 60 DOP content. At higher concentrations the loss peak is increased and T, is unaltered. Another absorption was observed at 100 Hz and at high temperatures, which was attributed to Maxwell-Wagner effect or direct current conductivity or both of them. It was found that the sample containing 40 parts DOP in 100 parts PVC possesses the best mechanical and electrical properties.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.