Phase change memory (PCM) is a rapidly growing technology that not only offers advancements in storage-class memories but also enables in-memory data processing to overcome the von Neumann bottleneck. In PCMs, data storage is driven by thermal excitation. However, there is limited research regarding PCM thermal properties at length scales close to the memory cell dimensions. Our work presents a new paradigm to manage thermal transport in memory cells by manipulating the interfacial thermal resistance between the phase change unit and the electrodes without incorporating additional insulating layers. Experimental measurements show a substantial change in interfacial thermal resistance as GST transitions from cubic to hexagonal crystal structure, resulting in a factor of 4 reduction in the effective thermal conductivity. Simulations reveal that interfacial resistance between PCM and its adjacent layer can reduce the reset current for 20 and 120 nm diameter devices by up to ~ 40% and ~ 50%, respectively. These thermal insights present a new opportunity to reduce power and operating currents in PCMs.

As the length scales of materials decrease, the heterogeneities associated with interfaces become almost as important as the surrounding materials. This has led to extensive studies of emergent electronic and magnetic interface properties in superlattices1–9. However, the interfacial vibrations that affect the phonon-mediated properties, such as thermal conductivity10,11, are measured using macroscopic techniques that lack spatial resolution. Although it is accepted that intrinsic phonons change near boundaries12,13, the physical mechanisms and length scales through which interfacial effects influence materials remain unclear. Here we demonstrate the localized vibrational response of interfaces in strontium titanate–calcium titanate superlattices by combining advanced scanning transmission electron microscopy imaging and spectroscopy, density functional theory calculations and ultrafast optical spectroscopy. Structurally diffuse interfaces that bridge the bounding materials are observed and this local structure creates phonon modes that determine the global response of the superlattice once the spacing of the interfaces approaches the phonon spatial extent. Our results provide direct visualization of the progression of the local atomic structure and interface vibrations as they come to determine the vibrational response of an entire superlattice. Direct observation of such local atomic and vibrational phenomena demonstrates that their spatial extent needs to be quantified to understand macroscopic behaviour. Tailoring interfaces, and knowing their local vibrational response, provides a means of pursuing designer solids with emergent infrared and thermal responses.

High thermal conductivity materials show promise for thermal mitigation and heat removal in devices. However, shrinking the length scales of these materials often leads to significant reductions in thermal conductivities, thus invalidating their applicability to functional devices. In this work, we report on high in-plane thermal conductivities of 3.05, 3.75, and 6 μm thick aluminum nitride (AlN) films measured via steady-state thermoreflectance. At room temperature, the AlN films possess an in-plane thermal conductivity of ∼260 ± 40 W m–1 K–1, one of the highest reported to date for any thin film material of equivalent thickness. At low temperatures, the in-plane thermal conductivities of the AlN films surpass even those of diamond thin films. Phonon–phonon scattering drives the in-plane thermal transport of these AlN thin films, leading to an increase in thermal conductivity as temperature decreases. This is opposite of what is observed in traditional high thermal conductivity thin films, where boundaries and defects that arise from film growth cause a thermal conductivity reduction with decreasing temperature. This study provides insight into the interplay among boundary, defect, and phonon–phonon scattering that drives the high in-plane thermal conductivity of the AlN thin films and demonstrates that these AlN films are promising materials for heat spreaders in electronic devices.

Materials with tunable thermal properties enable on-demand control of temperature and heat flow, which is an integral component in the development of solid-state refrigeration, energy scavenging, and thermal circuits. Although gap-based and liquid-based thermal switches that work on the basis of mechanical movements have been an effective approach to control the flow of heat in the devices, their complex mechanisms impose considerable costs in latency, expense, and power consumption. As a consequence, materials that have multiple solid-state phases with distinct thermal properties are appealing for thermal management due to their simplicity, fast switching, and compactness. Thus, an ideal thermal switch should operate near or above room temperature, have a simple trigger mechanism, and offer a quick and large on/off switching ratio. In this study, we experimentally demonstrate that manipulating phonon scattering rates can switch the thermal conductivity of antiferroelectric PbZrO3 bidirectionally by −10% and +25% upon applying electrical and thermal excitation, respectively. Our approach takes advantage of two separate phase transformations in PbZrO3 that alter the phonon scattering rate in different manners. In this study, we demonstrate that PbZrO3 can serve as a fast (<1 second), repeatable, simple trigger, and reliable thermal switch with a net switching ratio of nearly 38% from ~1.20 to ~1.65 W m−1 K−1.

Photoconductive PbSe thin films are highly important for mid-infrared imaging applications. However, the photoconductive mechanism is not well understood so far. Here we provide additional insight on the photoconductivity mechanism using transmission electron microscopy, x-ray photoelectron microscopy, and electrical characterizations. Polycrystalline PbSe thin films were deposited by a chemical bath deposition method. Potassium iodide (KI) was added during the deposition process to improve the photoresponse. Oxidation and iodization were performed to sensitize the thin films. The temperature-dependence Hall effect results show that a strong hole–phonon interaction occurs in oxidized PbSe with KI. It indicates that about half the holes are trapped by KI-induced self-trapped hole centers ( V k center), which results in increasing dark resistance. The photo Hall effect results show that the hole concentration increases significantly under light exposure in sensitized PbSe, which indicates the photogenerated electrons are compensated by trapped holes. The presence of KI in the PbSe grains was confirmed by I 3 d 5 / 2 core-level x-ray photoelectron spectra. The energy dispersive x-ray spectra obtained in the scanning transmission electron microscope show the incorporation of iodine during the iodization process on the top of PbSe grains, which can create an iodine-incorporated PbSe outer shell. The iodine-incorporated PbSe releases electrons to recombine with holes in the PbSe layer so that the resistance of sensitized PbSe is about 800 times higher than that of PbSe without the iodine-incorporated layer. In addition, oxygen found in the outer shell of PbSe can act as an electron trap. Therefore, the photoresponse of sensitized PbSe is from the difference between the high dark resistance (by KI addition and iodine incorporation) and the low resistance after IR exposure due to electron compensation (by electron traps at grain boundary and electron–hole recombination in KI hole traps).

This work studies the thermal conductivity and phonon scattering processes in a series of n‐type lead telluride‐lead selenide (PbTe–PbSe) nanostructured thin films grown by atomic layer deposition (ALD). The ALD growth of the PbTe–PbSe samples in this work results in nonepitaxial films grown directly on native oxide/Si substrates, where the Volmer–Weber mode of growth promotes grains with a preferred columnar orientation. The ALD growth of these lead‐rich PbTe, PbSe, and PbTe–PbSe thin films results in secondary oxide phases, along with an increase microstructural quality with increased film thickness. The compositional variation and resulting point and planar defects in the PbTe–PbSe nanostructures give rise to additional phonon scattering events that reduce the thermal conductivity below that of the corresponding ALD‐grown control PbTe and PbSe films. Temperature‐dependent thermal conductivity measurements show that the phonon scattering in these ALD‐grown PbTe–PbSe nanostructured materials, along with ALD‐grown PbTe and PbSe thin films, are driven by extrinsic defect scattering processes as opposed to phonon–phonon scattering processes intrinsic to the PbTe or PbSe phonon spectra. The implication of this work is that polycrystalline, nanostructured ALD composites of thermoelectric PbTe–PbSe films are effective in reducing the phonon thermal conductivity, and represent a pathway for further improvement of the figure of merit (ZT), enhancing their thermoelectric application potential.

Integrated nanophotonics is an emerging research direction that has attracted great interests for technologies ranging from classical to quantum computing. One of the key-components in the development of nanophotonic circuits is the phase-change unit that undergoes a solid-state phase transformation upon thermal excitation. The quaternary alloy, Ge2Sb2Se4Te, is one of the most promising material candidates for application in photonic circuits due to its broadband transparency and large optical contrast in the infrared spectrum. Here, we investigate the thermal properties of Ge2Sb2Se4Te and show that upon substituting tellurium with selenium, the thermal transport transitions from an electron dominated to a phonon dominated regime. By implementing an ultrafast mid-infrared pump-probe spectroscopy technique that allows for direct monitoring of electronic and vibrational energy carrier lifetimes in these materials, we find that this reduction in thermal conductivity is a result of a drastic change in electronic lifetimes of Ge2Sb2Se4Te, leading to a transition from an electron-dominated to a phonon-dominated thermal transport mechanism upon selenium substitution. In addition to thermal conductivity measurements, we provide an extensive study on the thermophysical properties of Ge2Sb2Se4Te thin films such as thermal boundary conductance, specific heat, and sound speed from room temperature to 400 °C across varying thicknesses.

No abstract