PurposeThe aim of the paper is the study of the change in the mechanical properties (and in particular in ductility), with the microstructure, of a biomedical Ti‐6Al‐4V alloy produced by different variants of selective laser melting (SLM).Design/methodology/approachTi‐6Al‐4V alloy produced by different variants of SLM has been mechanically characterized through tensile testing. Its microstructure has been investigated by optical observation after etching and by X‐ray diffraction analysis.FindingsSLM applied to Ti‐6Al‐4V alloy produces a material with a martensitic microstructure. Some microcracks, due the effect of incomplete homologous wetting and residual stresses produced by the large solidification undercooling of the melt pool, are observable in the matrix. Owing to the microstructure, the tensile strength of the additive manufactured parts is higher than the strength of hot worked parts, whereas the ductility is lower. A pre‐heating of the powder bed is effective in assisting remelting and reducing residual stresses, but ductility does not increase significantly, since the microstructure remains martensitic. A post‐building heat treatment causes the transformation of the metastable martensite in a biphasic a‐b matrix, with a morphology that depends on the heat treatment. This results in an increase in ductility and a reduction in strength values.Originality/valueThe study evidenced how it is possible to obtain a fully dense material and make the martensite transform in Ti‐6Al‐4V alloy through the variation of the SLM process. The stabilization of the microstructure also results in an improvement of the ductility.
PurposeThe purpose of this paper is the microstructural and mechanical characterization of a biomedical Ti‐6Al‐4V alloy produced by electron beam melting, and the study of the stability of the as‐built microstructure upon heat treatment.Design/methodology/approachTi‐6Al‐4V alloy produced by electron beam melting has been mechanically characterized through tensile and fatigue testing. Its microstructure has been investigated by optical observation after etching and by X‐ray diffractometry analysis. The stability of the microstructure of the as‐built material has been deepened carrying out suitable heat treatments, after an analysis by dilatometry test.FindingsThe microstructure of a Ti‐6Al‐4V alloy produced by electron beam melting has a very fine and acicular morphology, because of the intrinsically high‐solidification rate of the process. This microstructure is very stable, and the traditional thermal treatments cannot modify it; the microstructure changes significantly only when an amount of strain is introduced in the material. However, the mechanical properties of the alloy produced by electron beam melting are good.Originality/valueThe paper provides evidence of the microstructural stability of the material produced by electron beam melting. Even if the microstructure of the as‐built material is not recommended by the specific ISO standard, the related mechanical properties are fully satisfactory. This is a significant indication from the point of view of the production of Ti‐6Al‐4V orthopaedic and dental prostheses by electron beam melting.
Selective laser melting (SLM) is a rapid prototyping technique based on melting and solidification of powder layers to build up a 3-D solid body. [1][2][3] It was developed as a prototyping technology, but is attracting ever-increasing interest as a rapid manufacturing technology for the production, for instance, of orthopedic prostheses made of titanium and cobalt alloys [4,5] and die inserts made of low alloys and maraging steels for the plastics industry. [6,7] Because of the large solidification undercooling, SLM results in the formation of either very fine or metastable microstructures, which sometimes do not find a correspondence in the alternative technologies and in the international standards, as in the case of titanium alloys. [8] An in-depth investigation on the effect of the microstructure on mechanical properties is necessary to evaluate whether or not such a peculiar microstructure is acceptable for practical applications.SLM is used for the production of surgical tools, as well. In this case, a stainless steel combining mechanical strength, wear resistance and corrosion resistance is the best choice. This requirement is satisfied by the precipitation-hardening (PH) stainless steels. Among them, the 17-4 PH grade is a high-chromium steel with a martensitic microstructure (resulting from the transformation of austenite on cooling), which has to be heat treated (solution annealing and aging) to promote the precipitation of Cu phases. [9] In this material, the large solidification undercooling may prevent the formation of martensite in the as-built material, leading to a metastable austenitic microstructure.Metastable austenite may transform into martensite on straining, resulting in the well-known transformation-induced plasticity (TRIP) phenomenon. TRIP is exploited in some steel grades, namely the low alloyed Si-Mn steels as well as the high alloyed Mn-Si-Al steels, to improve their plastic ductility in cold forming. TRIP is also displayed by austenitic stainless steels. Its occurrence depends on the stacking fault energy (SFE) of austenite: [10] on decreasing SFE, deformation occurs by perfect and partial dislocation gliding, by twinning and then by martensitic transformation. With a SFE below 15-20 mJ m À2 , austenite transforms to e and a' martensite, resulting in an increase in strain hardenability and, in turn, ductility.An increase in toughness due to the presence of retained austenite in a 17-4 PH stainless steel was reported by Nakagawa and Miyazaki; [11] up to 30% austenite was stabilized in the microstructure by a special heat treatment. However, a mostly austenitic 17-4 PH stainless steels has never been investigated.In this paper, a study on the microstructure of a 17-4 PH stainless steels, produced by SLM, and on its effect on the tensile properties is presented. The as-built microstructure contains a large amount of metastable austenite. Tensile tests show a large plastic ductility coupled to significant strain hardenability, resulting in a high tensile strength around 1 GPa. The trans...
The compression Young's modulus and strength of lattice structures with porosity between 47.8% and 82.6% produced by Selective Laser Melting (SLM) of a Ti6Al4V powder were investigated. The Young's modulus and yield strength range from 1 GPa to 20 GPa and from 10 MPa to 250 MPa, respectively. On increasing porosity, both stiffness and strength decrease. When porosity increases above 60-65%, the strength shows an accentuated decrease compared to the stiffness decrease. The absence of struts parallel to the loading direction in the lattice structure allows to achieve higher yield strength than other structures having the same Young's modulus.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.