In this article, polylactic acid-based composites reinforced with 5% of polyethylene, iron, and magnesium powders were prepared by extrusion and compressed under the pressure of about 10 MPa and characterized. These composites were mechanically, thermally, and morphologically evaluated. It was found, compared to the pure polylactic acid (PLA), an improvement in tensile strength (both σ and YS0.2) was obtained for the composite with the iron powder addition, while the magnesium powder slightly improved the ductility of the composite material (from 2.0 to 2.5%). Degradation studies of these composites in the 0.9% saline solution over a period of 180 days revealed changes in the pH of the solution from acidic to alkaline, in all samples. The most varied mass loss was observed in the case of the PLA-5%Mg sample, where initially the sample mass increased (first 30 days) then decreased, and after 120 days, the mass increased again. In the context of degradation phenomenon of the tested materials, it turns out that the most stable is the PLA composite with the Fe addition (PLA-5%Fe), with highest tensile strength and hardness.

In this work two austenitic stainless steels, REX734 and 316LV were tested in terms of their microstructure and corrosion properties. The REX734 is a newer generation stainless steel, with modified chemical composition, in comparison to the 316LV grade. Potentiodynamic study of corrosion resistance was conducted in physiological saline solution (0.9% NaCl solution). In spite of the similarities of microstructure, grain size and phase structure in both materials, the corrosion tests revealed that the REX734, with lower nickel and higher nitrogen content, had better corrosion resistance than 316LV. Repassivation potential in the REX734 was almost six times higher than for the 316LV steel. Superior corrosion resistance of the REX734 steel was also confirmed by surface observations of both materials, since bigger and more densely distributed pits were detected in 316LV alloy.

No abstract

An influence of the powder metallurgy route on the phase structure, mechanical properties, and corrosion resistance of Fe–18%Cr–12%Mn–N nickel-free austenitic stainless steel as a potential material for medical applications were studied. The powder was mechanically alloyed in a high purity nitrogen atmosphere for 90 h followed by Hot Isostatic Pressing at 1150 °C (1423 K) and heat treatment at 1175 °C (1423 K) for 1 h in a vacuum with furnace cooling and water quenching. More than 96% of theoretical density was obtained for the samples after Hot Isostatic Pressing that had a direct influence on the tensile strength of the tested samples (Ultimate Tensile Strength is 935 MPa) with the total elongation of 0.5%. Heat treatment did not affect the tensile strength of the tested material, however, an elongation was improved by up to 3.5%. Corrosion properties of the tested austenitic stainless steel in various stages of the manufacturing process were evaluated applying the anodic polarization measurements and compared with the austenitic 316LV stainless steel. In general, the heat treatment applied after Hot Isostatic Pressing improved the corrosion resistance. The Hot Isostatic Pressing sample shows dissolution, while heat treatment causes a passivity range, the noblest corrosion potential, and lower current density of this sample.