This paper investigates the microstructure and the mechanical properties of β-tricalcium phosphate (β-TCP) three-dimensional (3D) porous materials reinforced with 45S5 bioactive glass (BG). β-TCP and β-TCP/x%-BG scaffolds with interconnected pores networks, suitable for bone regeneration, were fabricated by gel-casting method. Mechanical properties, porosity, and morphological characteristics were evaluated by compressive strength test, scanning electron microscopy (SEM) and X-ray microtomography analysis, whereas the structures were fully explored by XRD, and Raman spectroscopy. To the best of our knowledge, this is the first time where the mechanism for understanding the effect of bioglass on the mechanical properties and microstruture of β-TCP/45S5-BG scaffolds has been systematically studied. The findings showed that ionic product lixiviated from 45S5 bioactive glass, rich in silicon species and sodium ion, catalyzes a phase transition from β-TCP to Si-TCP by replacement of phosphorus for silicon and contributes to the improvement of scaffolds mechanical properties. The compressive strength of β-TCP/5%-BG and β-TCP/7.5%-BG was improved around 200% in comparison to pure β-TCP. Osteoblast-like cells (MG 63) were exposed to the materials for 24h through the use of medium conditioned by β-tricalcium phosphate/bioactive glass. Cell viability was measured by MTT assay in the cells and the data obtained were submitted to ANOVA, Tukey׳s multiple comparison (p<0.05). The β-TCP/7.5-BG promoted an increase of cell proliferation. The results suggest that compositions and processing method studied may provide appropriate materials for tissue engineering.
Polymer membranes have been widely used in guided tissue regeneration (GTR) and guided bone regeneration (GBR). The literature recognizes that poly (lactic acid) (PLA)/poly (ε-caprolactone) (PCL) blends have better physicochemical properties and that a porous polymer surface facilitates cell adhesion and proliferation. In addition, hydroxyapatite (HAp) incorporated into the polymer matrix promotes osteoinduction properties and osteoconduction to the polymer-ceramic biocomposite. Therefore, polymer membranes of PLA/PCL blend with the addition of HAp could be an alternative to be used in GBR. HAp was obtained by precipitation using the mixture of solutions of tetrahydrate calcium nitrate and monobasic ammonium phosphate salts. The porous membranes of the PLA/PCL (80/20) blend with the addition of HAp were obtained by solvent casting with a controlled humidity method, with the dispersion of HAp in chloroform and subsequent solubilization with the components of the blend. The solution was poured into molds for solvent evaporation under a controlled humidity atmosphere. The membranes showed the formation of pores on their surface, together with dispersed HAp particles. The results showed an increase in the surface porosity and improved bioactivity properties with the addition of HAp. Moreover, in biological studies with cell culture, it was possible to observe that the membranes with HAp have no cytotoxic effect on MC3T3 cells. These results indicate a promising use of the new biomaterial for GBR.
The austenitic stainless steel 316L is the most used metallic biomaterials in orthopedics applications, especially in the manufacture of articulated prostheses and as structural elements in fracture fixation, since it has high mechanical strength. However, because it is biologically inactive, it does not form chemical bond with bone tissue, it is fixed only by morphology. The development of biocomposites of stainless steel with a bioactive material, such as hydroxyapatite -HA, is presented as an alternative to improve the response in the tissue-implant interface. However significant reductions in mechanical properties of the biocomposite can occur. Different compositions of the biocomposite stainless steel 316L/HA (5, 20 and 50 wt. (%) HA) were prepared by mechanical alloying. After milling the powders for 10 hours, the different compositions of the biocomposite were compacted isostatically and sintered at 1200 °C for 2 hours. The mechanical properties of the biocomposites were analyzed by compression tests. The powders and the sintered composites were analyzed by scanning electron microscopy (SEM) and X-ray diffraction (XRD).
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.