The use of self-adhesive resin cements is an option for bonding fiber-reinforced composite posts to root canal dentin. Traditional resin cements apparently provide higher bond strengths than self-etch resin cements. Because of this, the bond strength of self-adhesive resin cements to root dentin should be evaluated. SUMMARYObjectives: This study evaluated the bond strength of luting systems for bonding glass fiber posts to root canal dentin. The hypothesis tested was that there are no differences in bond strength of glass fiber posts luted with different cement systems.Methods: Forty bovine incisors were randomly assigned to five different resin cement groups (n=8). After endodontic treatment and crown removal, translucent glass fiber posts were bonded into the root canal using five different luting protocols (self-cured cement and etchand-rinse adhesive system; dual-cured cement and etch-and-rinse adhesive system; self-cured cement and self-etch adhesive system; dualcured cement and self-etch adhesive system; and dual-cured self-adhesive cement). Pushout bond strength was evaluated at three different radicular levels: cervical, middle,

The purpose of this study was to investigate the influence of chlorhexidine (CHX) concentration on the microtensile bond strength (muTBS) of contemporary adhesive systems. Eighty bovine central incisors were used in this study. The facial enamel surface of the crowns was abraded with 600-grit silicon carbide paper to expose flat, mid-coronal dentin surfaces. The tested materials were Scotchbond Multipurpose (SMP), Single-Bond (SB), Clearfil SE Bond (CSEB) and Clearfil Tri S Bond (CTSB). All the materials were applied according to manufacturer's instructions and followed by composite application (Z250). The teeth were randomly divided into 16 groups: for the etch-and-rinse adhesives (SMP and SB), 0.12% or 2% CHX was applied prior to or after the acid etching procedure. For the self-etch adhesives (CSEB and CTSB) 0.12% or 2% CHX was applied prior to the primer. Control groups for each one of the adhesive systems were also set up. The specimens were immediately submitted to muTBS testing and the data were analyzed using Analysis of Variance and the Tukey post hoc test (alpha = .01). The failure patterns of the specimens were observed using scanning electron microscopy. The effects of 2% CHX were statistically significant (p < 0.01) for the self-etch adhesives but were not significant for the etch-and-rinse adhesive systems. Analysis of the data demonstrated no statistical difference between the etch-and-rinse adhesive systems. CHX-based cavity disinfectants in concentrations higher than 0.12% should be avoided prior to the self-etch adhesive systems evaluated in this study to diminish the possibilities of reduction in bond strength.

No abstract

SPC and SP led to equal reduction on fracture resistance of dental crowns, regardless of being mixed with water or 20% HP.

No abstract