A series of polymeric biomaterials including poly (methyl acrylate) (PMA), chitosan (CHT), poly(ethyl acrylate) (PEA), poly(hydroxyethyl acrylate) (PHEA), and a series of random copolymers containing ethyl acrylate and hydroxyethyl acrylate monomeric units were tested in vitro as culture substrates and compared for their impact on the proliferation and expansion of Schwann cells (SCs). Immunocytochemical staining assay and scanning electron microscopy techniques were applied to perform a quantitative analysis to determine the correct maintenance of the cultured glial cells on the different biomaterials. The results strongly suggest that cell attachment and proliferation is influenced by the substrate's surface chemistry, and that hydrophobic biomaterials based on PMA, PEA, and the copolymers PEA and PHEA in a narrow composition window are suitable substrates to promote cell attachment and proliferation of SCs in vitro.
Blends of polycaprolactone (PCL) and chitosan (CHT) were prepared by casting from a solution. CHT and PCL were dissolved by using acetic acid/water mixtures. Both solutions were slowly mixed to cast blend films containing 10%, 20%, 30%, and 40% by weight of CHT. PCL and CHT form phase separated blends. The phase morphology is in large extent controlled by the casting procedure. Even if casting of the film starts from a clear solution, the solvent composition determines the form in which phase separation takes place and consequently the morphology of the resulting blend after solvent evaporation. The blend containing 20% CHT presents cocontinuous phases. The sample presents a high elastic modulus even at temperatures above melting of PCL. Blends with higher CHT contents consist of disperse PCL domains in a CHT matrix and the contrary occurs in the blend containing 10% CHT in which disperse CHT domains with a network morphology appear inside the spherulites of PCL. In all the blends, the nucleation effect of CHT accelerates the crystallization of PCL from the melt, although in the blends with high CHT contents a part of the PCL mass included in large domains might not be affected by the presence of CHT. The sample containing 20% CHT has a peculiar behavior with respect to the crystallization of PCL, only a small part of PCL crystallizes in isothermal treatments although this fraction crystallizes faster than in the rest of the blends.
Bone Marrow mesenchymal stem cells can be induced to differentiate into osteoblasts to regenerate damaged bone tissue using tissue engineering techniques. In this study, we examine the use of chitosan scaffolds with double pore structure prepared by an innovative method that combines freeze gelation (that produces micropores) and particle leaching out technique (that produces interconnected spherical macropores) seeking to enhance the osteogenic differentiation of goat bone marrow stromal cells (GBMSCs). The double pore architecture of the scaffold was characterized by scanning electron microscopy (SEM), microcomputed tomography and confocal laser scanning microscopy. The obtained hierarchical pore structure allowed very efficient seeding of GBMSCs that are able to occupy the whole volume of the scaffold, showing good adhesion and proliferation. GBMSCs were differentiated into osteoblasts as indicated by alkaline phosphatase activity and osteocalcin expression. The results of this study demonstrate that chitosan scaffold may be promising biomaterial for bone regeneration.
A three-dimensional (3D) scaffolding system for chondrocytes culture has been produced by agglomeration of cells and gelatin microparticles with a mild centrifuging process. The diameter of the microparticles, around 10 μ, was selected to be in the order of magnitude of the chondrocytes. No gel was used to stabilize the construct that maintained consistency just because of cell and extracellular matrix (ECM) adhesion to the substrate. In one series of samples the microparticles were charged with transforming growth factor, TGF-β1. The kinetics of growth factor delivery was assessed. The initial delivery was approximately 48 % of the total amount delivered up to day 14. Chondrocytes that had been previously expanded in monolayer culture, and thus dedifferentiated, adopted in this 3D environment a round morphology, both with presence or absence of growth factor delivery, with production of ECM that intermingles with gelatin particles. The pellet was stable from the first day of culture. Cell viability was assessed by MTS assay, showing higher absorption values in the cell/unloaded gelatin microparticle pellets than in cell pellets up to day 7. Nevertheless the absorption drops in the following culture times. On the contrary the cell viability of cell/TGF-β1 loaded gelatin microparticle pellets was constant during the 21 days of culture. The formation of actin stress fibres in the cytoskeleton and type I collagen expression was significantly reduced in both cell/gelatin microparticle pellets (with and without TGF-β1) with respect to cell pellet controls. Total type II collagen and sulphated glycosaminoglycans quantification show an enhancement of the production of ECM when TGF-β1 is delivered, as expected because this growth factor stimulate the chondrocyte proliferation and improve the functionality of the tissue.
Blends of polycaprolactone (PCL) and chitosan (CHT) were prepared by casting from the mixture of solutions of both components in suitable solvents. PCL, and CHT, form phase separated blends with improved mechanical properties and increased water sorption ability with respect to pure PCL. The morphology of the system was investigated by scanning electron microscopy (SEM), atomic force microscopy (AFM) and confocal microscopy. Dispersed domains of CHT in the semicrystalline PCL matrix were found in samples with less than 20% CHT but cocontinuous phase morphologies are found in blends with 20% or more CHT. This feature was corroborated by the temperature dependence of the elastic modulus measured by dynamic mechanical properties as a function of temperature. It was observed that for those blends above 20 wt% CHT, the mechanical stability of the system was kept even after melting of the PCL phase. Primary human chondrocytes were cultured on the different substrates. Cell morphology was studied by SEM and the viability and proliferation was investigated by the colorimetric MTT assay. Different protein conformations were found by AFM on CHT and PCL samples which were related to the biological performance of the substrates. Hydrophilicty of the material is not directly related to the biological response and the sample with 20 wt% CHT shows better results than the other blends with respect to chondrocyte viability and proliferation. However, the results obtained in the blends are worse than in pure PCL. It seems to be correlated with the surface energy of the different blends rather than hydrophilicity.
The use of chitosan microparticles as injectable carriers for cell transplantation represents a promising alternative to avoid the drawbacks of the implantation of other forms of three-dimensional (3D) scaffolds seeded with cells. In this study, a 3D construct is obtained in vitro by combining chitosan microparticles crosslinked with genipin and goat bone marrow stromal cells (GBMCs). Cell viability and the morphology of GBMCs were evaluated after culture for 7 and 14 days. Our results show the feasibility of chitosan microparticles as potential injectable scaffolds for tissue engineering and regenerative medicine.
The aim of this study is to show the favorable effect of simple dynamic culture conditions on chondrogenesis of previously expanded human chondrocytes seeded in a macroporous scaffold with week cell-pore walls adhesion. We obtained enhanced chondrogenesis by the combination of chitosan porous supports with a double micro- and macro-pore structure and cell culture in a stirring bioreactor. Cell-scaffold constructs were cultured under static or mechanically stimulated conditions using an intermittent stirred flow bioreactor during 28 days. In static culture, the chondrocytes were homogeneously distributed throughout the scaffold pores; cells adhered to the scaffold pore walls, showed extended morphology and were able to proliferate. Immunofluorescense and biochemical assays showed abundant type I collagen deposition at day 28. However, the behavior of chondrocytes submitted to mechanical stimuli in the bioreactor was completely different. Mechanical loading influenced cell morphology and extracellular matrix composition. Under dynamic conditions, chondrocytes kept their characteristic phenotype and tended to form cell aggregates surrounded by a layer of the main components of the hyaline cartilage extracellular matrix, type II collagen, and aggrecan. An enhanced aggrecan and collagen type II production was observed in engineered cartilage constructs cultured under stirred flow compared with those cultured under static conditions.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.