A comprehensive structural and electrical characterization of solution-processed blend films of 6,13-bis(triisopropylsilylethynyl) pentacene (TIPS-pentacene) semiconductor and poly(alpha-methylstyrene) (PalphaMS) insulator was performed to understand and optimize the blend semiconductor films, which are very attractive as the active layer in solution-processed organic thin-film transistors (OTFTs). Our study, based on careful measurements of specular neutron reflectivity and grazing-incidence X-ray diffraction, showed that the blends with a low molecular-mass PalphaMS exhibited a strong segregation of TIPS-pentacene only at the air interface, but surprisingly the blends with a high molecular-mass PalphaMS showed a strong segregation of TIPS-pentacene at both air and bottom substrate interfaces with high crystallinity and desired orientation. This finding led to the preparation of a TIPS-pentacene/PalphaMS blend active layer with superior performance characteristics (field-effect mobility, on/off ratio, and threshold voltage) over those of neat TIPS-pentacene, as well as the solution-processability of technologically attractive bottom-gate/bottom-contact OTFT devices.
An organosilicate polymer, based on N,N'-diphenyl-N,N'-bis(4-((E)-2-(triethoxysilyl)vinyl)phenyl)biphenyl-4,4'-diamine (TEVS-TPD) with extended conjugation between the Si atom and the aromatic amine, was prepared under mild conditions via sequential Heck and sol-gel chemistry and used as an alternative to poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS), the most widely used planarizing hole injection/transport layer in solution-processed organic electronic devices. Spin-coating TEVS-TPD polymer solutions yield defect-free, uniform, thin films with excellent adhesion to the ITO electrode. Upon thermal cross-linking at 180 °C, the cross-linked polymer exhibits excellent solvent resistance and electrochemical stability. Solution-processed organic light emitting diode (OLED) devices using iridium-based triplet emitting layers and cross-linked TEVS-TPD films as a hole injection/transport layer show significantly improved performance including lower leakage current, lower turn-on voltage, higher luminance, and stability at high current density, as compared to the control device prepared with PEDOT:PSS.
The low frequency noise of individual ZnO nanowire (NW) field effect transistors (FETs) exposed to air is systematically characterized. The measured noise power spectrum shows a classical 1/f type. The noise amplitude is independent of source-drain current and inversely proportional to gate voltage. The extracted Hooge's constant of ZnO NW is found to be 6.52× 10 -3 . In addition, the low frequency noise of ZnO NW according to NW resistance and contact property are investigated. The noise amplitude is proportional to the square of ZnO NW resistance. If a sample shows a nonlinear current-voltage (I-V) characteristic due to a poor electrical contact, the noise power spectrum is proportional to the third power of current instead of the square of current.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.