Due to the relatively poor cell-material interaction of alginate hydrogel, alginate-gelatin crosslinked (ADA-GEL) hydrogel was synthesized through covalent crosslinking of alginate di-aldehyde (ADA) with gelatin that supported cell attachment, spreading and proliferation. This study highlights the evaluation of the physico-chemical properties of synthesized ADA-GEL hydrogels of different compositions compared to alginate in the form of films. Moreover, in vitro cell-material interaction on ADA-GEL hydrogels of different compositions compared to alginate was investigated by using normal human dermal fibroblasts. Viability, attachment, spreading and proliferation of fibroblasts were significantly increased on ADA-GEL hydrogels compared to alginate. Moreover, in vitro cytocompatibility of ADA-GEL hydrogels was found to be increased with increasing gelatin content. These findings indicate that ADA-GEL hydrogel is a promising material for the biomedical applications in tissue-engineering and regeneration.
The chain conformation of thin polymer films was investigated via diffuse neutron scattering. The samples consist of blend films of protonated and deuterated polystyrene spin coated onto glass substrates. A variation of the thickness of the blend films in a range of about 41 down to 0.66 times the radius of gyration R g of the chains in the bulk enables the determination of film thickness and confinement effects. With diffuse neutron scattering in a reflection geometry the chain conformation in thin polymer films with film thicknesses less than 20 nanometers could be investigated. With decreasing film thickness d below approximately 6 R g the in-plane dimension of the chains starts to increase which is caused by distortion of the chain conformation along the direction parallel and perpendicular to the surface of the film. This increase is quite significant below d < Rg and can be compared to theoretical predictions and simulations.
Inorganic scaffolds with high interconnected porosity based on bioactive glasses and ceramics are prime candidates for applications in bone tissue engineering. These materials however exhibit relatively low fracture strength and high brittleness. A simple and effective approach to improve the toughness is to combine the basic scaffold structure with polymer coatings or through the formation of interpenetrating polymer-bioactive ceramic microstructures. The polymeric phase can additionally serve as a carrier for growth factors and therapeutic drugs, thus adding biological functionalities. The present paper reviews the state-of-the art in the field of polymer coated and infiltrated bioactive inorganic scaffolds. Based on the notable combination of bioactivity, improved mechanical properties and drug or growth factor delivery capability, this scaffold type is a candidate for bone and osteochondral regeneration strategies. Remaining challenges for the improvement of the materials are discussed and opportunities to broaden the application potential of this scaffold type are also highlighted.
In this study biomimetic poly(glycerol sebacate) PGS matrix was developed for cardiac patch application. The rationale was that such matrices would provide conducive environment for the seeded cells at the interphase with PGS. From the microstructural standpoint, PGS was fabricated into dense films and porous PGS scaffolds. From the biological aspect, biomimetic PGS membranes were developed via covalently binding peptides Tyr-Ile-Gly-Ser-Arg (YIGSR) and Gly-Arg-Gly-Asp-Ser-Pro (GRGDSP), corresponding to the epitope sequences of laminin and fibronectin, respectively onto the surface. To improve and enhance homogenous binding of peptides onto the PGS surface, chemical modification of its surface was carried out. A sequential regime of alkaline hydrolysis with 0.01 M NaOH for 5 min and acidification with 0.01 M HCl for 25s was optimal. More COOH chemical group was exposed without causing deleterious effect on the bulk properties of the polymer as revealed by the physicochemical analysis carried out. HPLC analysis, chemical imaging and ToF-SIMS were able to establish the successful homogenous functionalization of PGS membranes with the peptides. Finally, the developed biomimetic membranes supported the adhesion and growth of rat and human cardiac progenitor cells.
The phase behavior of poly(styrene-b-butyl methacrylate), PS-b-PBMA, diblock copolymers was investigated by small-angle neutron scattering (SANS), neutron reflectometry (NR), and rheology. For a symmetrical P(dS-b-nBMA) diblock copolymer a lower critical order transition (LCOT) at 155°C was found by SANS and rheology. Furthermore, the temperature-dependent interaction parameter was determined in the temperature regime between 110 and 145°C from fits to the scattering curves in the disordered region. The interaction parameter increases with increasing temperature and shows a weak temperature dependence. The LCOT behavior thus is expected to be a large entropic contribution to . The interfacial width observed by NR is relatively large compared to other diblock copolymers. Different block copolymers were investigated with respect to the influence of miscibility on tensile properties. While poly(styrene-b-butyl methacrylate) diblock copolymers show significant synergistic effects on tensile properties, for poly(methyl methacrylate-b-butyl methacrylate) diblock copolymers no significant synergistic effects on tensile properties were observed due to the increased interaction parameter and the smaller interfacial width as compared to the case of PS-b-PBMA diblock copolymers.
Many different biofabrication approaches as well as a variety of bioinks have been developed by researchers working in the field of tissue engineering. A main challenge for bioinks often remains the difficulty to achieve shape fidelity after printing. In order to overcome this issue, a homogeneous pre-crosslinking technique, which is universally applicable to all alginate-based materials, was developed. In this study, the Young’s Modulus after post-crosslinking of selected hydrogels, as well as the chemical characterization of alginate in terms of M/G ratio and molecular weight, were determined. With our technique it was possible to markedly enhance the printability of a 2% (w/v) alginate solution, without using a higher polymer content, fillers or support structures. 3D porous scaffolds with a height of around 5 mm were printed. Furthermore, the rheological behavior of different pre-crosslinking degrees was studied. Shear forces on cells as well as the flow profile of the bioink inside the printing nozzle during the process were estimated. A high cell viability of printed NIH/3T3 cells embedded in the novel bioink of more than 85% over a time period of two weeks could be observed.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.