A 3.5 nm amorphous CoFeB film was sputtered on GaAs (001) wafer substrate without applying magnetic field during deposition, and a significant in-plane uniaxial magnetic anisotropy (UMA) field (Hu) of about 300 Oe could be achieved. To precisely determine the intrinsic Gilbert damping constant (α) of this film, both ferromagnetic resonance (FMR) and time-resolved magneto-optical Kerr effect (TRMOKE) techniques were utilized. With good fitting of the dynamic spectra of FMR and TRMOKE, α is calculated to be 0.010 and 0.013, respectively. Obviously, the latter is 30% larger than the former, which is due to the transient heating effect during the TRMOKE measurement. In comparison with ordinary amorphous CoFeB films with negligible magnetic anisotropies, α is enhanced significantly in the CoFeB/GaAs(001) film, which may be mainly resulted from the enhanced spin-orbit coupling induced by the CoFeB/GaAs interface. However, the significant in-plane UMA plays minor role in the enhancement of α.
Abstract:Magnetization damping is a key parameter to control the critical current and the switching speed in magnetic random access memory, and here we report the effect of the growth sequence on the magnetic dynamics properties of perpendicularly magnetized Ta/CoFeB/MgO structures. Ultrathin CoFeB films have been grown between Ta and MgO but with different stack sequences, i.e. substrate/Ta/CoFeB/MgO/Ta and substrate/Ta/MgO/CoFeB/Ta. The magnetization dynamics induced by femtosecond laser was investigated by using all-optical pump-probe measurements. We found that the Gilbert damping constant was modulated by reversing stack structures, which offers the potential to tune the damping parameter by the growth sequence. The Gilbert damping constant was enhanced from 0.017 for substrate/Ta/CoFeB/MgO/Ta to 0.027 for substrate/Ta/MgO/CoFeB/Ta. We believe that this enhancement originates from the increase of intermixing at the CoFeB/Ta when the Ta atom layer was grown after the CoFeB layer.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.