We report stable, high performance zinc oxide thin film transistors grown by an atmospheric pressure atomic layer deposition system. With all deposition and processing steps kept at or below 200°C, the alumina gate dielectric shows low leakage (below 10−8A∕cm2) and high breakdown fields. Zinc oxide thin film transistors in a bottom gate geometry yield on/off ratios above 108, near zero turn-on voltage, little or no hysteresis, and mobility greater than 10cm2∕Vs. With alumina passivation, shifts in threshold voltage under gate bias stress compare favorably to those reported in the literature.
The Hubble Space Telescope made systematic observations of the split comet P/Shoemaker-Levy 9 (SL9) (P designates a periodic comet) starting in July 1993 and continuing through mid-July 1994 when the fragments plunged into Jupiter's atmosphere. Deconvolutions of Wide Field Planetary Camera images indicate that the diameters of some fragments may have been as large as approximately 2 to 4 kilometers, assuming a geometric albedo of 4 percent, but significantly smaller values (that is, < 1 kilometer) cannot be ruled out. Most of the fragments (or nuclei) were embedded in circularly symmetric inner comae from July 1993 until late June 1994, implying that there was continuous, but weak, cometary activity. At least a few nuclei fragmented into separate, condensed objects well after the breakup of the SL9 parent body, which argues against the hypothesis that the SL9 fragments were swarms of debris with no dominant, central bodies. Spectroscopic observations taken on 14 July 1994 showed an outburst in magnesium ion emission that was followed closely by a threefold increase in continuum emission, which may have been caused by the electrostatic charging and subsequent explosion of dust as the comet passed from interplanetary space into the jovian magnetosphere. No OH emission was detected, but the derived upper limit on the H2O production rate of approximately 10(27) molecules per second does not necessarily imply that the object was water-poor.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.